<For high demand large-sized or medium-sized precision plastic mold and alloy parts.>
1.International Standard
| GB | DIN | ASIA | JIS |
| 3Cr2MnNi | 1.2311 | P20 | PDS-S |
2.Chermical Compisition(Wt%) :
| 1.2311 | C | Si | Mn | Cr | Mo | S | P |
| 0.35-0.45 | 0.20-0.40 | 0.60-1.00 | 1.80-2.10 | 0.30-0.55 | ≤0.003 | ≤0.003 |
3.Available Size(mm) :
| Flat Bar Size | Round Bar Size(mm) | ||||
| Thickness | Width | Length | Diameter | Length | |
| 10-700 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 | |
4.Product Technique:
Introduction:
Low-carbon mold steels or group P steels are of different types that include P2, P3, P4, P5, P6, P20, and P21 steels. Chromium and nickel are the main alloying elements found in group P steels.
P20 tool steels are nitrided or carburized. These steels are capable of being machined into complex and large dies and molds. P20 steels are mostly used in the carburized condition. The presence of chromium and nickel enhances the toughness and hardness of P20 steels.
Fabrication and Heat Treatment:
| Tempering: | P20 tool steels are tempered at 482-593°C (900 to 1100°F) for a Rockwell C hardness of 28 to 34. |
| Annealing: | Annealing takes place at 760-788°C (1400 to 1450°F) and then the steels are cooled slowly in the furnace at a temperature less than 4°C (40°F) per hour. |
| Cold Working: | P20 tool steels are capable of being readily cold worked by using conventional tooling methods with the alloy in the annealed condition. |
| Welding: | Conventional methods are used for welding of P20 tool steels. |
| Forging: | P20 tool steels are forged at 1093°C (2000°F) down to 899°C (1650°F). Forging below 871°C (1600°F) is not recommended for these steels. |
| Forming: | P20 tool steels can be readily formed by conventional methods in the annealed condition. |
| Machinability: | P20 tool steels have excellent machinability at about 80% that of water hardening steels. |
| Heat Treatment: | P20 tool steels are heated to 871-899°C (1600-1650°F) in the carburizing medium during the carburizing process. After being carburized, these steels are heated to 816-871°C (1500-1600°F) in order to be hardened and then held for 15 minutes and finally oil quenched. |
| Applications: | P20 tool steels are used for low-temperature applications that include injection molds and die casting dies. |
5.Feature:
1.Vacuum degassing refining processing steel purity, suitable for polishing or etch processing plastic mold.
2. In pre-harden state delivery, no need for heat treatment can be directly used for mold processing, shorten the construction.
3. After heat treatment machining and polishing performance is good, the nitriding treatment, can be suitable for chrome plating surface treatment, such as material is the qualitative hardness is uniform (400mm thick), good toughness and good machining performance.
4.Good hardness uniformity and polishing property, good machining properties.
5.Good integral mechanical performance under high temperatures.
6.Good heat-resistance and fatigue-resistance.
7. Pre-hardened to HRC30-36 can be directly used for mold processing, shorten the construction period.
Delivery Time
1) For abundant stock, 7-15 days.
2) For customized products, 15-30 days.
Loading Details:
FAQ:
Q1: What do you do for the control of the quality?
A1: Before loading into the container, our products will all be inspected by ultrasonic inspection. Quality Grade conforms to SEP 1921-84 E/e, D/d, C/c as per customer's request.
Q2:: What are your hot-selling products?
A2: D2/1.2379, H13/1.2344, CR12MOV, DC53, CR8, abundant stock for both plates and rounds. Competitive prices and short lead-time.
Q3: Can we visit your company and factory?
A3: Yes, warmly welcome! We can book the hotel for you before you come to China and arrange our driver to our airport to pick you up when you come.
Q4: Are you a manufacturer or merely a trader?
A4: We are a group of companies and owned manufacturer bases and trading companies. We specialized in plastic mold steel, hot work mold steel, cold work mold steel, alloy steel for mechanical, high-speed steel, etc. All materials are of high quality and competitive price.