Product Description
TJ 2215 Acrylic Resin
Acrylic resin agent is a resin glue composed of powder and liquid, that is, composed of acrylic powder and liquid curing agent.
The acrylic powder is white powder, the curing agent is colorless to light green transparent liquid. After mixing the curing agent and acrylic powder for 10-15 minutes at room temperature (20-25°C), it can be cured into a transparent or translucent hard material, and the material can be ground and polished. It is suitable for various materials, especially in the electronic industry such as PCB and SMT. No special equipment is required, and it is easy and fast to operate at room temperature. It has the advantages of low heat release during mounting, small thermal shrinkage, good weather fastness and good wear resistance.
Acrylic resin agent is a resin glue composed of powder and liquid, that is, composed of acrylic powder and liquid curing agent.
The acrylic powder is white powder, the curing agent is colorless to light green transparent liquid. After mixing the curing agent and acrylic powder for 10-15 minutes at room temperature (20-25°C), it can be cured into a transparent or translucent hard material, and the material can be ground and polished. It is suitable for various materials, especially in the electronic industry such as PCB and SMT. No special equipment is required, and it is easy and fast to operate at room temperature. It has the advantages of low heat release during mounting, small thermal shrinkage, good weather fastness and good wear resistance.
Fast mounting, smooth and translucent;
Low viscosity, excellent flow properties;
Excellent permeability to small pores and depressions;
Good support for the slices after mounting;
High hardness after mounting;
Suit with all currently known soft or hard plastic molds;
Low exotherm, peak temperature <70°C (12g, room temperature 20-22°C).
| Mixing ratio (by weight) | 10:7 (resin powder: curing agent) * |
| Mounting time (22-25ºC) | 10-15 minutes* |
| Operation time | 3-5min @ 100 g |
| Peak temperature | 70ºC* |
| Hardness | 82D |
| Chemical properties | Insoluble in water (after curing) |
| Contractility | ≤0.6% |
| Edge protection | Better |
| Transmittance | ≥33% |