Constantan( UALLOY 049)
(Common Name: CuNi45, NC50.Cuprothal, Alloy 294, Cuprothal 294, Nico, MWS-294, Cupron, Copel, Alloy 45, Neutrology, Advance, CuNi 102, Cu-Ni 44, Konstantan,constantan.)
UALLOY049 is a copper-nickel alloy (Cu56Ni44 alloy) characterized by high electrical resistance, high ductility and good corrosion resistance. It is suitable for use at temperatures up to 400°C Typical applications for UALLOY49 are temperature-stable potentiometers, industrial rheostats and electric motor starter resistances.
The combination of negligible temperature coefficient and high resistivity makes the alloy particulary suitable for the winding of precision resistors. UALLOY049 is manufactured from electrolytic copper and pure nickel. In finer wire sizes the alloy is designated as UALLOY49TC(Thermocouple).
Normal composition%
Corrosion resistance performance
Style of supply
(Common Name: CuNi45, NC50.Cuprothal, Alloy 294, Cuprothal 294, Nico, MWS-294, Cupron, Copel, Alloy 45, Neutrology, Advance, CuNi 102, Cu-Ni 44, Konstantan,constantan.)
UALLOY049 is a copper-nickel alloy (Cu56Ni44 alloy) characterized by high electrical resistance, high ductility and good corrosion resistance. It is suitable for use at temperatures up to 400°C Typical applications for UALLOY49 are temperature-stable potentiometers, industrial rheostats and electric motor starter resistances.
The combination of negligible temperature coefficient and high resistivity makes the alloy particulary suitable for the winding of precision resistors. UALLOY049 is manufactured from electrolytic copper and pure nickel. In finer wire sizes the alloy is designated as UALLOY49TC(Thermocouple).
Normal composition%
| Nickel | 45 | Manganese | 1 |
| Copper | Bal. |
Typical Mechanical properties(1.0mm)
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 250 | 420 | 25 |
Typical Physical properties
| Density (g/cm3) | 8.9 |
| Electrical resistivity at 20ºC (ohm*mm2/m) | 0.49 |
| Temperature factor of resistivity(20ºC~600ºC)X10-5/ºC | -6 |
| Conductivity coefficient at 20ºC (WmK) | 23 |
| EMF vs Cu(μV/ºC )(0~100ºC ) | -43 |
| Coefficient of thermal expansion | |
| Temperature | Thermal Expansion x10-6/K |
| 20 ºC- 400ºC | 15 |
| Specific heat capacity | |
| Temperature | 20ºC |
| J/gK | 0.41 |
| Melting point (ºC) | 1280 |
| Max continuous operating temperature in air (ºC) | 400 |
| Magnetic properties | non-magnetic |
Corrosion resistance performance
| Alloys | Working In atmosphere at 20ºC | Working at max temperature 200ºC | ||||
| Air and oxygen contain gases | gases with Nitrogen | gases with sulfur oxidability | gases with sulfur reductibility | carburization | ||
| UALLOY049 | good | good | good | good | bad | good |
Style of supply
| Alloys Name | Type | Dimension | |
| UALLOY049W | Wire | D=0.03mm~8mm | |
| UALLOY049R | Ribbon | W=0.4~40 | T=0.03~2.9mm |
| UALLOY049S | Strip | W=8~200mm | T=0.1~3.0 |
| UALLOY049F | Foil | W=6~120mm | T=0.003~0.1 |
| UALLOY049B | Bar | Dia=8~100mm | L=50~1000 |