Product Description
Copper and Copper alloy welding
Cusi3 SG -CUSI3 Silicon Copper / Copper Alloy Tig /MIG Welding Wire Welding Material
| CHEMICAL COMPOSITION(%) | |||||||||||||
| Standard | Class | Alloy | Cu | Al | Fe | Mn | Ni | P | Pb | Si | Sn | Zn | Other |
| ISO24373 | Cu6560 | CuSi3Mn1 | bal. | 0.02 | 0.5 | 0.5~ 1.5 | - | 0.05 | 0.02 | 2.8~ 4.0 | 0.2 | 0.4 | 0.5 |
| GB/T9460 | SCu6560 | CuSi3Mn | bal. | max 0.01 | max 0.5 | max 1.5 | - | - | max 0.02 | 2.8~ 4.0 | max 1.0 | max 1.0 | max 0.5 |
| BS EN14640 | Cu6560 | CuSi3Mn1 | bal. | 0.01 | 0.5 | 0.5~ 1.5 | - | 0.02 | 0.02 | 2.8~ 4.0 | 0.2 | 0.2 | 0.4 |
| AWS A5.7 | C65600 | ERCuSi-A | bal. | 0.01 | 0.05 | 1.5 | - | - | 0.02 | 2.8~ 4.0 | 1.0 | 1.0 | 0.50 |
| DIN 1733 | 2.1461 | SG-CuSi3 | bal. | max 0.01 | max 0.3 | 0.5~ 1.5 | - | max 0.02 | max 0.02 | 2.8~ 4.0 | max 0.2 | max 0.2 | max 0.4 |
| TRADE MARK | S211 |
| Equivalent to AWS | ERCuSi-A |
| Characteristics | Good mechanical properties Good corrosion resistance |
| Welding Method | GTAW Argon arc welding |
| Application | Used for TIG,Excellent for plain or coated steels.Also used for sufacing arears subjected to corrossion. |
Best for butt and the hard facing of brass,especially for the MIG welding of zinc coated steel sheet.Pre-heat suggested when MIG hard facing for large size products and use pulsed argon arc welding while hard facing on steel.
| Physical Properties and Mechanical Properties: | |
| Solids-Temperature | 910ºC |
| Liquids-Temperature | 1025ºC |
| Density | 8.5kg/dm3 |
| Tensile Strength | 330-370N/mm2 |
| Elongation | 40% |
| Brinell Hardness | 80-95HB |
Our products are suitable for automobile casting, high pressure valve iron, hydraulic rod, marine casting, aerospace casting,ocean exploration, precision machinery, deep sea scale, marine water scale, high pressure valve, etc. Our company is a world leader in the field of copper alloys, and has made outstanding contributions to the field of copper alloy welding in the world.Our company has been to Arabia, Dubai, Germany, the United States, France, the Middle East, and Vietnam for many times to conduct academic exchanges and promote the world. Development in the field of copper alloy welding.