Customized Plastic Raw Material Extrusion Grade Polyamide 66 Pellets PA66 GF25 For Thermal Break Strips Production
Product Introduction:
Polyamide 6.6 granules reinforced by fiberglass, with special additives, is blended and extruded by twin screw extrusion machine. It is more suitable for extrusion of heat insulation strip. Compared with ordinary granules, it is more conducive to forming. It has certain advantages in speed, surface finish and yield. The performances of nylon insulating strip produced made of this material meet the national standards. It can not only be customized according to customer requirements, far exceeding the national standard, but also can add high-efficiency flame retardant to achieve the purpose of flame retardant.
Advantage:
1. It has excellent mechanical properties, high strength, high toughness.
2. The material has excellent coloring ability, can achieve various requirements of color matching
3. The shrinkage rate of PA66 is between 1% and 2%. The addition of glass fiber additives can reduce the shrinkage rate to 0.2%~1%. The shrinkage ratio is large in the flow direction and in the direction perpendicular to the flow direction.
4. PA66 is resistant to many solvents, but is less resistant to acids and other chlorinating agents.
5. PA66 excellent flame retardant performance, by adding different flame retardants can achieve different levels of flame retardant effect.
Polywell PA66 Granules Performance Table
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
Our Company:
Related Products we can provide:
Please feel free to contact us if you have any questions.
Product Introduction:
Polyamide 6.6 granules reinforced by fiberglass, with special additives, is blended and extruded by twin screw extrusion machine. It is more suitable for extrusion of heat insulation strip. Compared with ordinary granules, it is more conducive to forming. It has certain advantages in speed, surface finish and yield. The performances of nylon insulating strip produced made of this material meet the national standards. It can not only be customized according to customer requirements, far exceeding the national standard, but also can add high-efficiency flame retardant to achieve the purpose of flame retardant.
Advantage:
1. It has excellent mechanical properties, high strength, high toughness.
2. The material has excellent coloring ability, can achieve various requirements of color matching
3. The shrinkage rate of PA66 is between 1% and 2%. The addition of glass fiber additives can reduce the shrinkage rate to 0.2%~1%. The shrinkage ratio is large in the flow direction and in the direction perpendicular to the flow direction.
4. PA66 is resistant to many solvents, but is less resistant to acids and other chlorinating agents.
5. PA66 excellent flame retardant performance, by adding different flame retardants can achieve different levels of flame retardant effect.
PA66 GF25 is a 25 % glass fibre reinforced PA 66. It demonstrates outstanding mechanical properties such as higher strength, rigidity, creep strength and dimensional stability.
Polywell PA66 Granules Performance Table
| NO. | Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| Material Properties | ||||
| 1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| 2 | Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
| 3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| 4 | Melting point | ºC | ≥240 | ≥240 |
| 5 | Testing for tensile cracks | - | No cracks | No cracks |
| 6 | Shore hardness | - | 80±5 | 80-85 |
| 7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| 8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| 9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
| 10 | Elongation at break | % | ≥2.5 | ≥2.6 |
| 11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| 12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| 13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| 14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| 15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
About color:
The color of our products is black, but we also can customize according to customers' requirements.
The color of our products is black, but we also can customize according to customers' requirements.
Application:
Widely used in machinery, instrumentation, automotive parts, electrical and electronics, railways, household appliances, telecommunications, textile, sports and leisure goods, pipes and precision engineering products.
Widely used in machinery, instrumentation, automotive parts, electrical and electronics, railways, household appliances, telecommunications, textile, sports and leisure goods, pipes and precision engineering products.
Packaging & Delivery:
Packaging details: 25kg/bag
Delivery details: Shipped in 7-15 working days after deposit.
Packaging details: 25kg/bag
Delivery details: Shipped in 7-15 working days after deposit.
Our Company:
Related Products we can provide:
| Thermal Break Strip Extruding Machine | Thermal Break Strip | Granulator Machine |
Please feel free to contact us if you have any questions.
Address: Jinfeng Town, Zhangjiagang City, Jiangsu Province, China