Audited Supplier
200*2440mm, 200*3000mm
Grey
Non-asbestos
>1.3G/Cm3
Tobermorite Crystals;Cement ; Natural Fiber
<10%
<30%
<0.25%
<0.5%
>12MPa
<0.3W/M`K
a-Class Incombustible
240 Minutes
Wood Grain Siding Fiber Cement Board
Grade A
Panel
Fibre Board
Texture
Square
Square
Over 2000 ℃
Building
6-12mm
LUTAI
Wooden Pallets, 8 Wooden Pallets in 1X20gp
SGS, ISO, CE
Shandong Province
68118200
Product Description
wood grain wall panel
LuTai brand wooden grain siding panel adopts the high quality quartz sand, silicate, natural fiber, and a variety of selected mineral. With high temperature and high pressure. The product don't have any radioactivity and harmful elements. Belongs to new, green and environmental material. The surface with the typical natural cedar wood grain, appearance is natural and beautiful. Also can prevent the attack of white ant and sawteeth animals. The wooden grain siding panel has the feature of durability, flexibility and creativity, more stable and durable than wood products. Because of the lower cost and excellent properties, it is accepted by the foreign and domestic customers, also the best choice of all kinds of construction. When choose the coating material, we recommend environmental water-based paint. For example: water-based pure acrylic coating and so on.
Products characteristics
1. Light weight, structural earthquake-resistant.
2. Heat insulation.
3. Fire-proof for 4 hours , class-A1 incombustibility.
4. High strength, anti-bending strength more than 12MPA.
5. Well decoration effect, comfortable living function.
6. Green, environmental material.
7. Fast and simple construction, high efficiency, lower cost.
Size & specification
Thickness(mm):6mm-15mm.
Size :(mm): 200*2400mm, 1200*2400mm, other sizes according to the order .
Density: 1.3-1.5g/cm3.
Thermal conductivity: less than 0.3W/(M.K).
Water content: ≤10%.
Water absorption(plain): ≤30%.
Swelling rate: ≤0.25%.
Thermal shrinkage: ≤0.5%.
Anti-bending strength: ≥12MPA.
Water tightness:the reverse side allows showing water mark but not dropping after
24 hours.
Freezing resistance: it doesn't show break and layer after 25 times freeze thawing.
Impact resistance: without continuous crack after one shock.
Incombustibility: Class - A1
Recommend application
Exterior wall of Villa, apartment, office building, work shop, school and so on.
Old building renovation, interior decoration.
| Item | Fiber cement board | Gypsum Plaster Board | MagnesiumBoard | TKBoard(Glass Fiber Cment Board) |
| Raw Material | Cement ,Quartz Sand,Organic/Inorfil Cellulose Fiber | Gypsum,Paper | Magnesium Oxide,Magnesium Chloride | C-Glass,Short Mineral wool,Low Alkali Portland |
| Anti-Bending Strength(Mpa) | >12 | 4-5 | <12 | 6-8 |
| Fire-proof Rate | A-class incombustible(GB8624-1997) | Non-Flammable | Incombustible | Incombustible |
| Incombustibility(min) | >240 | 60 | 50 | 70 |
| Damp-proof Rate | After wetting, the strengthdrops by 20-40%,recovers by 100% after dryness | Distortion after wetting,beyond retrieve | Distortion after wetting,beyond retrieve | Distortion after wetting,beyond retrieve |
| Use Age | Used for many years | sagging because of absorbing the Moisture in the air,short lifetime | Sagging because of absorbing the Moisture in the air,short lifetime | Distortion after wetting,beyond retrieve, short lifetime |