Product Description
N06035 is an upgrade version of N06030. It has extraordinary resistance in the wet process phosphoric acid production environment, which is widely used in fertilizer production. Its performance in this environment is far superior to N06035 and stainless steels. It can also resist localized corrosion and chloride-induced stress corrosion cracking in chlorides containing media. Because of its high chromium content, N06035 is extremely resistant to other oxidizing acids, such as nitric acid and mixtures containing nitric acid. As a result of its appreciable molybdenum content, it possesses moderate resistance to reducing acids, and unlike other nickel-chromium-molybdenum alloys, it is very resistant to caustic dealloying in hot sodium hydroxide.
CHEMICAL COMPOSITION
CHEMICAL COMPOSITION
| C | Mn | Fe | P | S | Si | Cu | Ni | Co | Al | Ti | Cr | Nb+Ta | Mo | B | N | W | La | V | Nb | |
| Hastelloy B | ≤0.05 | ≤1.0 | 4.0-6.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | ≤1.0 | 26.0-30.0 | 0.2-0.4 | |||||||||
| Hastelloy B-2 | ≤0.01 | ≤1.0 | ≤2.0 | ≤0.02 | ≤0.03 | ≤0.01 | balance | ≤1.0 | 0.04-0.07 | 26.0-30.0 | ||||||||||
| Hastelloy C | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | 50.0-58.0 | 14.5-16.5 | 15.0-17.0 | |||||||||||
| Hastelloy C-4 | ≤0.015 | ≤1.0 | ≤3.0 | ≤0.04 | ≤0.03 | ≤0.08 | balance | ≤2.0 | ≤0.7 | 14.0-18.0 | 14.0-17.0 | |||||||||
| Hastelloy C-22 | ≤0.015 | ≤0.5 | 2.0-6.0 | ≤0.02 | ≤0.35 | ≤0.08 | balance | ≤2.5 | 20.0-22.5 | 12.5-14.5 | 2.5-3.5 | 0.02 | ||||||||
| Hastelloy C-276 | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | 14.5-16.5 | 15.0-17.0 | 3.0-4.5 | ≤0.35 | ||||||||
| Hastelloy C-2000 | ≤0.01 | ≤0.5 | ≤3.0 | ≤0.025 | ≤0.01 | ≤0.08 | 1.3-1.9 | balance | ≤2.0 | ≤0.5 | 22.0-24.0 | 15.0-17.0 | ||||||||
| Hastelloy G-30 | ≤0.03 | 0.3-1.5 | 13.0-17.0 | ≤0.04 | ≤0.02 | 0.2-0.8 | 1.0-2.4 | balance | ≤5.0 | 28.0-31.5 | 4.0-6.0 | 1.5-4.0 | 0.3-1.5 | |||||||
| Hastelloy G-35 | ≤0.05 | ≤0.5 | ≤2.0 | ≤0.03 | ≤0.015 | ≤0.6 | ≤0.30 | balance | ≤1.0 | ≤0.4 | 32.25-34.25 | 7.6-9.0 | ≤0.6 | ≤0.2 | ||||||
| Hastelloy X | 0.05-0.15 | ≤1.0 | 17.0-20.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | 0.5-2.5 | 20.5-23.0 | 8.0-10.0 | 0.2-1.0 | |||||||||
| Hastelloy S | ≤0.02 | 0.3-1.0 | ≤3.0 | ≤0.02 | ≤0.015 | 0.2-0.75 | balance | ≤2.0 | 0.1-0.5 | 14.5-17.0 | 14.0-16.5 | ≤1.0 | 0.01-0.1 |
THE MINIMUM MECHANICAL PROPERTIES AT NORMAL TEMPERATURE
| Alloy and State | Tensile Strength | Yield Strength | Rate of Elongation | Brinell Hardness |
| Rm N/mm2 | RP0.2N/mm2 | A5% | HB | |
| Hastelloy B | ≥760 | ≥350 | ≥40 | - |
| Hastelloy B-2 | ≥760 | ≥350 | ≥40 | - |
| Hastelloy C | 690 | 310 | 40 | - |
| Hastelloy C-4 | ≥690 | ≥276 | ≥40 | - |
| Hastelloy C-22 | ≥690 | ≥310 | ≥45 | - |
| Hastelloy C-276 | ≥690 | ≥283 | ≥40 | - |
| Hastelloy C-2000 | ≥690 | ≥283 | ≥45 | - |
| Hastelloy G-30 | ≥586 | ≥241 | ≥30 | - |
| Hastelloy X | ≥586 | ≥241 | ≥30 | - |
| Hastelloy S | ≥110 | ≥52 | ≥46 | - |