Yg15
84.5hra
14.0g/cm3
2800MPa
as Wear-Resistance
ZZUP
25kg. Carton
YG15C OD85*ID13.2*40 mm
Zhuzhou, Hunan, China
820900100
Product Description
Specifications
1. Grade: YG15C , 15% Co
2. YG8,YG6,YG3,YG10,YG15,YT14,YT5,YT05,YT15,YG20,YG25,YL10.2,YS2T,YG6X etc all kinds of grades for your choose.
3. Can product customize drawing,sizes and shape.
Products Show
Grades choosing
Common grades for all kinds metal
Grades for cold mill roll or hot mill roll steel
Common grades for all kinds metal
| Grade | Density g/cm3 | Hardnes HRA | T.R.S Mpa | Performance&application recommended |
| YG6A | 14.85 | 92.5 | 2000 | Fine grain alloy,good wear resistance.it is suitable for manufacturing forming cutter,wear-resistant parts etc. |
| YG8 | 14.7 | 89.8 | 2800 | High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc. |
| YG11 | 14.4 | 88.5 | 2900 | High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc. |
| YG15 | 14.0 | 87.0 | 3000 | Suitable for manufacturing punching dies, wear-resistant parts. |
| YG20 | 13.5 | 85.5 | 2800 | High bending strength,suitable for manufacturing progressive dies and other punching dies. |
| YG25 | 13.1 | 81.5 | 2950 | High bending strength,wear resistance lower than YM6A, suitable for manufacturing cutter ,wear-resistant parts etc. |
| YS2T | 14.25 | 92.0 | 2500 | Fine grain alloy, with high wear resistance, bending strength, bonding resistance and thermal strength. it is suitable for machining refractory alloys,stainless steel, high manganese steel, etc. |
Grades for cold mill roll or hot mill roll steel
| Grade | Wc (%) | Co (%) | Ni (%) | Cr (%) | Density g/cm3 | Hardness ≥HRA | T.R.S ≥Nmm2 | Compression Strength ≥Nmm2 | Thermal Expansivity 10-6/K | Thermal Conductivity W/cm.k | Young's Elastic Modulus KN/mm2 |
| YGR60 | 70 | 30 | 12.8 | 78 | 2200 | 2900 | 7 | ||||
| YGR55 | 76 | 24 | 13.1 | 80 | 2400 | 3000 | 6.8 | 0.17 | 420 | ||
| YGR45 | 80 | 20 | 13.5 | 81 | 2500 | 3100 | 6.4 | 0.14 | 480 | ||
| YGR40 | 82 | 18 | 13.7 | 82.5 | 2600 | 3200 | 6.2 | 0.2 | 530 | ||
| YGR30 | 85 | 15 | 14.2 | 84.8 | 2700 | 3300 | 6.1 | 0.2 | 530 | ||
| YGR25 | 88 | 12 | 14.3 | 85 | 2600 | 3400 | 6 | 0.2 | 550 | ||
| YGH55 | 74 | 26 | 12.9 | 80 | 2200 | 3000 | 7 | 0.17 | 450 | ||
| YGH45 | 75 | 25 | 13.4 | 82 | 2400 | 3100 | 6.5 | 0.18 | 480 | ||
| YGH40 | 82 | 18 | 13.6 | 83.5 | 2500 | 3200 | 6.4 | 0.19 | 500 | ||
| YGH30 | 85 | 15 | 13.9 | 83.5 | 2400 | 3300 | 6.1 | 0.2 | 540 | ||
| YGH25 | 88 | 12 | 14.1 | 85 | 2300 | 3400 | 6 | 0.2 | 560 |
Common sizes:
| Outdiameter (mm) | Inner diameter (mm) | Height (mm) | Outdiameter (mm) | Inner diameter (mm) | Height (mm) | |
| 90 | 51 | 4~100 | 125 | 45 | 4~100 | |
| 90 | 20 | 125 | 80 | |||
| 90 | 3 | 130 | 40 | |||
| 95 | 75 | 130 | 50 | |||
| 95 | 68.5 | 140 | 90 | |||
| 95 | 74 | 142 | 78 | |||
| 100 | 65 | 150 | 90 | |||
| 100 | 62.1 | 210 | 200 | |||
| 100 | 20 | 161 | 108 | |||
| 105 | 46 | 212 | 120 | |||
| 105 | 65.5 | 158.8 | 87.32 | |||
| 105 | 81 | 170.66 | 95 | |||
| 105 | 75 | 180 | 87.32 | |||
| 110 | 20 | 180 | 120.65 | |||
| 110 | 30 | 228.3 | 126 | |||
| 110 | 90 | 208 | 126 | |||
| 114 | 94 | 228 | 130 | |||
| 115 | 65 | 285 | 160 | |||
| 115 | 60 | 320 | 260 | |||
| 120 | 46 | 280 | 240 | |||
| 120 | 65 | 318 | 280 | |||
| 120 | 60 | 600 | 550 | |||
| 125 | 45 | 800 | 200 |
Other sizes can be offered as per customers' requirements
Packing details
Shipping ways
Production process
Packing details
Shipping ways
Production process