E71T-11, E71T-GS
Flux-cored Wire
Carbon Steel
Containing Flux
Acidic
10-20mm
TYUE
0.8/0.9/1.0/1.2/1.4/1.6/2.0/2.4mm
China
8311200000
Product Description
Wenzhou Tinayu Electronic Co., Ltd.
High Quality CO2 Gas shielded flux-cored welding wire
Model No: E71T-11, E71T-GS, E71T-1
Conforms to: AWS A5.20/ASME SFA A5.20
Diameter::0.8 0.9 1.0 1.2 1.6mm
Free sample OEM approved
Weld Process: Mig Welding Process
Application: for all position
Brand: Tyue
Product Description:
E71T serie sis a kind of TI type flux cored wire for CO2 welding. It has high cladding efficiency, good welding technical performance in all-position welding, apply for low carbon steel and 500MPA grade strength steel welding, such as Industry of Metallurgical, Building, Chemical, shipping, pressure vessels, mechanical equipments.
Packing & Delivery: AWS A5.20 E71T-1C, E71T-11, E71T-GS
Size(MM) × Weight (KG)
0.8MMX1KG/SPOOL,
0.8MMX5KG/SPOOL,
0.8MMX15KG/SPOOL,
0.9MMX1KG/SPOOL,
0.9MMX5KG/SPOOL,
0.9MMX15KG/SPOOL,
1.0MMX1KG/SPOOL,
1.0MMX5KG/SPOOL,
1.0MMX15KG/SPOOL,
1.2MMX1KG/SPOOL,
1.2MMX5KG/SPOOL,
1.2MMX15KG/SPOOL,
Advantage
• All-position with stable arc less splash
• Less welding smoke, shaped good appearance, high welding efficiency
• Inherent quality stable and reliable,good mechanical property of deposited metal
• Manufactured under a quality system certified to ISO 9001 requirements
Chemical Date of E71T-11
| Mechanical Properties of Deposited Metal of E71T-11 | ||||
| Test Item | Rm(MPa) | ReL or Rp0.2(Mpa) | A(%) | KV2(J) |
| Guarantee Value | ≥480 | ≥400 | ≥22 | ≥27(-20°C) |
| General Result | 580 | 480 | 27 | 128 |
| Chemical Composition of Deposited Metal (%)(CO2Shielding Gas) of E71T-11 | |||||||
| Chemical Composition | C | Si | Mn | P | S | Ni | Cu |
| General Result | 0.12 | 0.04 | 0.70 | 0.014 | 0.011 | 0.28 | 0.12 |
Chemical Date of E71T-GS
| Mechanical Properties of Deposited Metal of E71T-GS | ||||
| Test Item | Rm(MPa) | ReL or Rp0.2(Mpa) | A(%) | KV2(J) |
| Guarantee Value | ≥480 | ≥400 | ≥22 | ≥27(-20°C) |
| General Result | 580 | 480 | 27 | 128 |
| Chemical Composition of Deposited Metal (%)(CO2Shielding Gas) of E71T-GS | |||||||
| Chemical Composition | C | Mn | Si | S | P | Ni | Cu |
| General Result | 0.07 | 0.59 | 0.06 | 0.008 | 0.014 | 0.25 | 0.15 |
NOTE ON USAGES:Do not use shielding gas