Unsaturated Polyester Resin
27837-75-8
(C8h4o3.C4H2O3.C2h6o2)X
Carbon Chain Polymer
Light Yellow
CCS, Dnv
4 Drums
80drums
Hand Lay-up
TIANMA
220kg /Drum or 1000kg/ IBC
220kg/Drum
China
39079100
Product Description
https://membercenter.made-in-china.com/productmanage.do?xcase=view&prodId=PBqEkewVbTRp&queryGroupId=&queryCatCode=&pageSize=30&queryState=-1&prodUpgradeActivity=
2, Liquid resin technical data:
Gel Time: 50% cyclohexano peroxide 4%, Accelerator E1: 4%:
3, resin casting matrix performance
Remark: casting matrix should follow GB8237-87
Hardness system: hardener 55%MEKPO: 1.5% accelerator E1: 1%
60ºC× 3 Hours + 80ºC× 2 hours
The technical data of liquid resin:
TM-191RS UPR is a kind of general-purpose use UPR, low viscosity, good mechanical strength and high elongation. It can be
applied in all kinds of FRP products as well as lay-up products.2, Liquid resin technical data:
| item | unit | index | test standard |
| Appearance | -- | Clear pale yellow liquid | GB/T 8237.4.1.1 |
| viscosity | 25ºC, Pa.S | 0.25~0.45 | GB/T 7193.1 |
| gel time | 25ºC, min | 9-17 | GB/T 7193.6 |
| acid value | mgKOH/g | 25~30 | GB/T 2895 |
| non-volatile | % | 61~67 | GB/T 7193.3 |
3, resin casting matrix performance
| item | unit | measured value | test standard |
| Barcol Hardness | -- | 41 | GB 3854-83 |
| HDT | ºC | 70 | GB 1634-04 |
| Flexural Strength | MPa | 114 | GB/T 2570-95 |
| tensile strength | MPa | 60 | GB/T 2568-95 |
| Elongation at break | % | 3.5 | GB/T 2568-95 |
| Impact Strength | KJ/m2 | 10.2 | GB/T 2571-95 |
Hardness system: hardener 55%MEKPO: 1.5% accelerator E1: 1%
60ºC× 3 Hours + 80ºC× 2 hours
The technical data of liquid resin:
| 1: Hand lay-up General purpose | ||||||||||
| Code | Type | 25º C PA. S | Min | % | MPa | % | MPa | HDT | Application | |
| Viscosity | Gel time | Non-Volatile | Tensile | Elongation | Flexural | |||||
| Strength | Strength | |||||||||
| TM-189 | PA | 0.25-0.45 | 10-22 | 59-65 | 60 | 4 | 100 | 57 | Water resistance, for boat. CCS | |
| TM-191 | PA | 0.25-0.45 | 9-17 | 61-67 | 55 | 1.8 | 110 | 66 | Translucent, general FRP purpose | |
| TM-191RS | PA | 0.25-0.45 | 9-17 | 61-67 | 60 | 3.5 | 114 | 70 | For FRP product, general purpose | |
| TM-196 | PA | 0.60-1.20 | 9.1-18.9 | 64-70 | 76 | 2 | 120 | 72 | Flexibility, high strength, CCS | |
| TM-580 | IPA | 0.40-0.70 | 10-20 | 66-70 | 15 | 68 | 10 | 67 | Flexibilizer or flexible resin, with other resins | |
| TM-1032 | PA | 0.25-0.65 | 15-23 | 15-23 | 60 | 2 | 105 | 67 | Good mechanical property, for bus, boat, CCS approval | |
| TM-22 | PA | 0.34-0.38 | 16-22 | 16-22 | 62 | 2.3 | 108 | 65 | Pre-promoted, thixotropy and low shrinkage | |
| TM-2068 | PA | 0.20-0.40 | 10-25 | 11-25 | 58 | 1.5 | 110 | 100 | Hot water resistance and high HDT, for bathtub | |
| TM-10070 | PA | 0.30-0.34 | 8-18 | 8-18 | 65 | 2 | 115 | 68 | Low viscosity, rapid wetting reinforcement for high strength FRP products. | |