Product Description
AWS E6013
Welding Electrode for Mild Steel
AWS A5.1-2004: E6013
ASME SFA-5.1: E6013
BS EN ISO 2560-B-E 4313 A
GB/T5117 E4313
Introduction:
AWS E6013 is a kind of mild steel welding electrode, all position welding (except vertical down). It welds on AC or DC with excellent performance and easy re-strike features, as well as stable arc and beautiful appearance of weld.
Application:
Used for the mild steel. Especially suitable for sheet metal steel, tank welding and other types of welding which require a smooth and clean bead appearance.
Chemical Composition of Deposited Metal (%)
Mechanical Properties of Deposited Metal
X-ray Radiographic Inspection: Grade II
Size and Recommended Welding Current (AC or DC)
Notice: Normally the welding electrode does not need to be re-baked in case it is affected with damp seriously re-bake it at 150ºC for 30-60 minutes before use.
Packing: 5kg/box, 4boxes/carton, 50cartons/pallet. 21MT -26MT per 1X20" FCL.
Welding Electrode for Mild Steel
AWS A5.1-2004: E6013
ASME SFA-5.1: E6013
BS EN ISO 2560-B-E 4313 A
GB/T5117 E4313
Introduction:
AWS E6013 is a kind of mild steel welding electrode, all position welding (except vertical down). It welds on AC or DC with excellent performance and easy re-strike features, as well as stable arc and beautiful appearance of weld.
Application:
Used for the mild steel. Especially suitable for sheet metal steel, tank welding and other types of welding which require a smooth and clean bead appearance.
Chemical Composition of Deposited Metal (%)
| Item | C | Mn | Si | S | P |
| Guarantee Values | ≤0.12 | 0.3-0.6 | ≤0.35 | ≤0.035 | ≤0.040 |
| Typical Values | 0.07 | 0.38 | 0.27 | 0.021 | 0.022 |
Mechanical Properties of Deposited Metal
| Test Item | Tensile Strength RM(MPa) | Yield Strength ReL(MPa) | Elongation (%) | KV2 (J) | KV2 (J) |
| Guarantee Values | ≥420 | ≥330 | ≥17 | Normal Temperature | 0ºC |
| Typical Values | 480 | 380 | 29 | 50-80 | ≥47 |
X-ray Radiographic Inspection: Grade II
Size and Recommended Welding Current (AC or DC)
| Size (mm) | 2.0 X 300 | 2.5 X 300 | 3.2 X 350 | 4.0 X 400 | 5.0 X4 00 |
| Current (A) | 40-70 | 60-90 | 80-130 | 130-210 | 170-280 |
Notice: Normally the welding electrode does not need to be re-baked in case it is affected with damp seriously re-bake it at 150ºC for 30-60 minutes before use.
Packing: 5kg/box, 4boxes/carton, 50cartons/pallet. 21MT -26MT per 1X20" FCL.