Product Description
Grade A+ 1kg Casting Billet Material dental Nickel Chromium Porcelain Alloy
Vs Ni-1
Nickel chrome with beryllium for free,use for dental ceramic restorations
Vs Ni-2
A high strength nickel chrome with beryllium alloy,use for dental ceramic restorations
Compositon | Technical Specifications | Compositon | Technical Specifications | ||||||||
Nickel | 62% | Melting Range() | 1335±50 | Nickel | 70% | Melting Range() | 1335±50 | ||||
Chrome | 23% | Yield Strength(MPa) | 400 | Chrome | 18% | Yield Strength(MPa) | 880 | ||||
Molybdenum | 10% | Elongation(%) | 14 | Molybdenum | 8% | Elongation(%) | 3 | ||||
Silicon | 2% | RockwellHardness | 80 | Beryllium | 1.7% | Rockwell Hardness | 80 | ||||
Others | 3% | Coefficient Of Liner Expansion(25-500) | 14 | Others | 2% | Coefficient Of Liner Expansion(25-500) | 14 | ||||
Vs Co-1
A cobalt chrome alloy,nickel and beryllium free,use with ceramic restorations
Vs Co-3
A cobalt chrome alloy,for restoration of removeable framework and partial dentures
Compositon | Technical Specifications | Compositon | Technical Specifications | ||||||||
Cobalt | 60% | Melting Range() | 1360±50 | Cobalt | 50% | Melting Range() | 1350±50 | ||||
Chrome | 26% | Yield Strength(MPa) | 530 | Chrome | 25% | Yield Strength(MPa) | 620 | ||||
Wolfram | 10% | Tensile Strength(MPa) | 880 | Ferrum | 15% | Tensile Strength(MPa) | 810 | ||||
Molybdenum | 4% | Elongation(%) | 3 | Molybdenum | 5% | Elongation(%) | 3 | ||||
Others | 2% | Rockwell Hardness | 30 | Nickel | 4% | Rockwell Hardness | 30 | ||||
Coefficient Of Liner Expansion(25-500) | 14.7 | Others | 2% | ||||||||