Product Description
UT& Pre-Shaded & Multilayer | ||||||
Temperature rising | Temperature rising | Time Span | Total Time | |||
°C/min | °C | Hour | Hour | |||
0 | 20 | 0 | ||||
10 | 900 | 1.5 | 1.5 | |||
0 | 900 | 0.5 | 2 | |||
3.27 | 1470 | 2.8 | 4.8 | |||
0 | 1470 | 2 | 6.8 | |||
4.58 | 900 | 2 | 8.5 | |||
About Us
Vsmile is a china based dental consumables manufacturer which delivers solutions to dental laboratories. We have a professional sales & marketing team that provides our customers with effective service including inquiry handling, sample preparation, order processing, shipment and documentation. Meeting and exceeding our Customers' expectations is our goal.
Contact us today to findout how we can help you save money every month and keep your lab running at peak efficiency.With Vsmile's professional assistance,you can expect outstanding results.
Vsmile Zirconia Manufacturing process
The first operation is the axial pressing of the zirconia. Products are manufactured in standard shapes like discs, cylinders and blocks according to market requirements. It is however possible to comply with our customer's specific requirements and produce customized product shapes and dimensions.
Isostatic pressing method:
After axial pressing, during which the semi-finished parts are given their necessary consistency, an isostatic pressing process is performed on all the products. The isostatic pressing process ensures all parts have a homogenous density and shrinkage distribution. This guarantees that during and after the sintering process, the products will always have extremely constant material characteristics.
Mechanical processing method:
Following the isostatic pressing process, the semi-finished parts can be shaped or machined to achieve the preferred geometry in accordance with product specifications.
Pre-sintering process:
During this process, the semi-finished parts are sintered at a specific temperature that optimizes the subsequent processing stages. Specific, computer controlled kilns are used for the heating up, dwell and cooling down phases.
The shrinkage factor of each production batch is carefully determined in our laboratory. The use of this shrinkage factor ensures that during final sintering, finished parts will have the dimensions required.
The first operation is the axial pressing of the zirconia. Products are manufactured in standard shapes like discs, cylinders and blocks according to market requirements. It is however possible to comply with our customer's specific requirements and produce customized product shapes and dimensions.
Isostatic pressing method:
After axial pressing, during which the semi-finished parts are given their necessary consistency, an isostatic pressing process is performed on all the products. The isostatic pressing process ensures all parts have a homogenous density and shrinkage distribution. This guarantees that during and after the sintering process, the products will always have extremely constant material characteristics.
Mechanical processing method:
Following the isostatic pressing process, the semi-finished parts can be shaped or machined to achieve the preferred geometry in accordance with product specifications.
Pre-sintering process:
During this process, the semi-finished parts are sintered at a specific temperature that optimizes the subsequent processing stages. Specific, computer controlled kilns are used for the heating up, dwell and cooling down phases.
The shrinkage factor of each production batch is carefully determined in our laboratory. The use of this shrinkage factor ensures that during final sintering, finished parts will have the dimensions required.