WA / WA-B / WA-P / WA-R
Natural Corundum
Corundum Abrasives
Machinery
Surface Finish
Artificial Abrasives
Mill
Conventional Abrasive
White
Alpha- Al2O3
Hexagonal
9
More Than 3.90g/cm3.
Hv2200-2300
Polishing, Grind, Sand Blasting, Refractory.
kumthai
25kg P. P Bag+1mt Jumbo Bag, 25kg Paper Bag+Pallet
F8-F1200, P12-P2500, 0-1mm, 1-3mm,3-5mm,5-8mm, etc
Zhengzhou, China
2818109000
Product Description
High Quality White Aluminum Oxide Fused Alumina(WA/WA-B/WA-P/WA-R) Corundum Abrasives, Special Specifications Customizable!
White Fused Alumina (WA) is produced by bayer alumina in an electric arc furnace at high temperatures. The product shows higher hardness, higher bulk density and good cleanliness. The materials can be used to grind high carbon steel, high speed steel, chilled steel and so on. It can also be used as polishing materials and precision founding sand, spraying and coating materials, catalyst carrier, special ceramics and super refractory materials.
White Corundum/White Aluminum Oxide/White Fused Alumina are applied into many industrial fields due to its stable and great physical and chemical properties. It can be used for making bonded/coated abrasive tools, for grinding, polishing, lapping, blasting, precision casting, and refractory industry, aerospace industry, mobile phone and electronic industry, jewelry industry, hardware industry, ceramics, automobile parts, bearing, powder metallurgy and so on.
Note: Special requirements on chemical composition and other terms can be satisfied through discussion.
The grit sizes of White Corundum/White Aluminum Oxide/White Fused Alumina WA WFA are produced according to national standard and international standard, and can be also produced according to customers' requirements.
Note: Special requirements on chemical composition and other terms can be satisfied through discussion.
Product package: 25kg P. P Bag+1MT Jumbo Bag, 25kg Paper Bag+1 MT Pallet, or according to customers' requirements.
White Fused Alumina (WA) is produced by bayer alumina in an electric arc furnace at high temperatures. The product shows higher hardness, higher bulk density and good cleanliness. The materials can be used to grind high carbon steel, high speed steel, chilled steel and so on. It can also be used as polishing materials and precision founding sand, spraying and coating materials, catalyst carrier, special ceramics and super refractory materials.
White Corundum/White Aluminum Oxide/White Fused Alumina are applied into many industrial fields due to its stable and great physical and chemical properties. It can be used for making bonded/coated abrasive tools, for grinding, polishing, lapping, blasting, precision casting, and refractory industry, aerospace industry, mobile phone and electronic industry, jewelry industry, hardware industry, ceramics, automobile parts, bearing, powder metallurgy and so on.
| Grain Usages and Types | ||||
| Usage | For vitrified wheels | For organic wheels | For coated abrasives | For refractory materials |
| Type | WA | WA-B | WA-P | WA-R |
| Physical Characteristics | |||||
| Item | Basic mineral | Crystal system | Crystal color | Mohs hardness | Density |
| White aluminum oxide | α- Al2O3 | Hexagonal | White | 9 | ≥3.90g/cm3 |
| Item | Micro hardness | Electrical resistivity | Grinding ability(compared with diamond as one) | Linear expansion coefficient(when 900ºC α•10-6k-1) | |
| White aluminium oxide | HV2200-2300 | 1014-1016Ω•cm | 0.12 | 8.3 | |
| Chemical Composition | |||
| GB/T 2479-2008 | |||
| Type | Grit | Chemical composition (%, by weight) | |
| Al2O3 | Na2O | ||
| WA | F4-F80 | ≥99.10 | ≤0.35 |
| F90-F150 | ≥99.10 | ≤0.40 | |
| F180-F220 | ≥98.60 | ≤0.50 | |
| F230-F800 | ≥98.30 | ≤0.60 | |
| F1000-F1200 | ≥98.10 | ≤0.70 | |
| WA-B | F4-F80 | ≥99.00 | ≤0.50 |
| F90-F150 | ≥99.00 | ≤0.60 | |
| F180-F220 | ≥98.50 | ≤0.60 | |
| WA-P | P12-P80 | ≥99.10 | ≤0.35 ≤0.40 |
| P100-P150 | ≥99.10 | ||
| P180-P220 | ≥98.60 | ≤0.50 | |
| P240-P800 | ≥98.30 | ≤0.60 | |
| P1000-P1200 | ≥98.10 | ≤0.70 | |
| P1500-P2500 | ≥97.50 | ≤0.90 | |
| WA-R | 0-1mm | ≥99.00 | ≤0.50 |
| 1-3mm | ≥99.00 | ≤0.50 | |
| 3-5mm | ≥99.00 | ≤0.50 | |
| 5-8mm | ≥99.00 | ≤0.50 | |
The grit sizes of White Corundum/White Aluminum Oxide/White Fused Alumina WA WFA are produced according to national standard and international standard, and can be also produced according to customers' requirements.
| Chemical Composition | |||||
| GB/T 2479v-2008 | |||||
| Type | Grit Size | Bulk Density | Whiteness | Chemical composition (%, by weight) | |
| Al2O3 | Na2O | ||||
| WA | F120-F220 | ≥1.80g/cm3 | ≥80% | ≥99.10 | ≤0.40 |
Product package: 25kg P. P Bag+1MT Jumbo Bag, 25kg Paper Bag+1 MT Pallet, or according to customers' requirements.