Audited Supplier
RTV2030, MCSIL-2030
Synthetic Rubber
Silicone Rubber
Liquid
Liquid Rubber
RTV2030
White
100:2~100:5
25000cps
30 Shore a
30~40mins
4~6hrs
3.8 MPa
30n/mm
480%
0.3%
12 Months Under 25 Celsius Degree
MC silicone
25kg, 200kg/Can
SGS, ROHS, MSDS, REACH
China
3910000
Product Description
Item No. | Properties before curing | Curing | ||||||||
| Part A | Part B | Part A+ Part B | Pot life at 250C | De-molding Time at 25ºC | ||||||
| Appearance | Appearance | Ratio | Viscosity | |||||||
| MCSIL-2030 | White | Clear | 100:2 | 25000±20000 cps | 30-40 mins | 4-6 hours | ||||
| Properties after curing 24 hours | ||||||||||
| Hardness Shore A | Tear strength | Tensile Strength | Elongation break (%) | Linear Shrinkage | ||||||
| 30 | 28-30 N/mm | 3.8 Mpa | 450-500 | 0.2-0.4% | ||||||
RTV-2 tin cure liquid silicone rubber is a two component material, and it consist of Part A base silicone and Part B curing agent. When the two parts mix together and pour or brush on a object, the silicone base and curing agent can cure to be a silicone mold at room temperature; And 24 hours later, the silicone mold can be released from the object, and then the silicone mold can be poured into the following material to copy: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...
FEATURES
1.Good flowability
2.Long working time
3. Medium hardness
4. High tear and tensile strength
5. Easy de-mould from complex replica parts
6. Acid and alkali-resistance
7. Low linear shrinkage
APPLICATION
Mold making for poly resin crafts, PU crafts, PU resin crafts,plastic toy,
gypsum crafts, large-scale cement mold, artificial fossils ,building decoration materials,
Wax, Soap and candles crafts,
Note:
Silicone MCSIL series is an industrial product and must not be used in food contact and dental human skin molding applications.
PROCEDURES
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
PACKING:
Part A :20kg/drum, 25kg/drum or 200kg/drum of silicone rubber
Part B :0.8kg/bottle, 1kg/bottle of silicone rubber