E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
Steel Alloy
2.0-5.0
300-450
Carbon Structural Steel
High Potassium Titanium
Acidic
Chromium Stainless Steel
Surfacing Electrode, Low Hydrogen Type Electrode, High Efficient Iron Powder Electrode, Gravity Electrode
AC, DC+
Electrode Diameter(mm) 2.0 2.5 3.2 4.0
Average 30 Days
T/T; L/C; Western Union
Low Price
Standard Export
WGHX
5kg/Box, 20kg/Carton, 1mt/ Pallet Neutral Packing
AWS E6013, GB E4313
China
Product Description
Description:
AWS E6013 is a low-carbon steel electrode with a high potassium titanium coating and can be used on A. C. Or D. C. It has excellent welding technological properties. The arc is stable. The spatter is small. The slag viscosity is moderate. It can be used freely. The slag is easy to clean. The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel, such as ships, vehicles, building, and general machinery.
Chemical composition of deposited metal(%)
C Mn Si S P
≤ 0.10 0.32-0.55 ≤ 0.30 ≤ 0.035 ≤ 0.04
Mechanical Properties of Deposited Metal
Rm(MPa) Rel(MPa) A(%) AKV(J)0º C
≥ 420 ≥ 330 ≥ 17 ≥ 27
Welding reference current(AC, DC+)
Electrode diameter(mm) 2.0 2.5 3.2 4.0
Welding current 50-80 60-100 100-140 150-210
Chemical Composition of Deposited Metal(%)
Mechanical Properties of Deposited Metal
Reference Current(AC,DC)
website: https://wghongxing88.en.made-in-china.com/
AWS E6013 is a low-carbon steel electrode with a high potassium titanium coating and can be used on A. C. Or D. C. It has excellent welding technological properties. The arc is stable. The spatter is small. The slag viscosity is moderate. It can be used freely. The slag is easy to clean. The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel, such as ships, vehicles, building, and general machinery.
Chemical composition of deposited metal(%)
C Mn Si S P
≤ 0.10 0.32-0.55 ≤ 0.30 ≤ 0.035 ≤ 0.04
Mechanical Properties of Deposited Metal
Rm(MPa) Rel(MPa) A(%) AKV(J)0º C
≥ 420 ≥ 330 ≥ 17 ≥ 27
Welding reference current(AC, DC+)
Electrode diameter(mm) 2.0 2.5 3.2 4.0
Welding current 50-80 60-100 100-140 150-210
Chemical Composition of Deposited Metal(%)
Chemical Composition | C | Mn | Si | S | P |
Guarantee Value | ≤0.12 | 0.3~0.6 | ≤0.35 | ≤0.035 | ≤0.040 |
Mechanical Properties of Deposited Metal
Test Item | Rm(MPa) | ReL(Mpa) | A(%) | KV2(J) | KV2(J) |
Guarantee Value | ≥420 | ≥330 | ≥17 | -(normal temperature) | -(0°C) |
General Result | 460~540 | ≥340 | 18~26 | 50~80 | ≥47 |
Reference Current(AC,DC)
Electrode diameter(mm) | Φ2.5 | Φ3.2 | Φ4.0 | Φ5.0 |
Welding current(A) | 50~90 | 90~130 | 130~210 | 170~210 |