Product Description
Description
PA6 1013B is copolymerization for injection molding with the safety
And reliability of the excellent stability.
Application
The product is used for making used in auto parts, power tools,
Electrical outlet, building materials
| Physical property | Rating | Test method |
| Density | 1.14 g/cm3 | |
| MFR(230 ºC,2.16KG) | 15.49g/10min | GB/T 3682-2000 |
| Mechanical property | Rating | Test method |
| Tensile strength | 59.21MPa | GB/T 1040-1992 |
| Elongation at break | 123.67/v50% | GB/T 1040-1992 |
| Flexural strength | 68.79 MPa | GB/T 9341-2000 |
| Flexural modulus | 1.51GPa | GB/T 9341-2000 |
| Impact property | Rating | Test method |
| Charpy Notched Impact Strength | 29.51KJ/m2 | GB/T 1043-1993 |
| Charpy impact strength | 25JNBKJ/m2 | GB/T 1043-1993 |
| Other property | Rating | Test method |
| Relative viscosity deviation | <0.02WT% | |
| Relative viscosity | 2.75 | |
| Viscosity | 2.81 | GB/T 1632-1993 |
| Water content | 0.06WT% | |
| Tio2content | 0-1.3WT% | |
| NOTE ISO 9001 2000 | ||
| Typical properties: these are not to be construed as specifications | ||