Reaction Bonded sic is sintered by adding the free silicon (content is less than 12%) into the reaction sintering sub-micron silicon carbide powder in 1500 ºC vacuum sintering furnace. Company produces silicon carbide material with excellent stability and wear resistance under high and low temperature, high speed, half dry friction working condition. The maximum overall sealing ring can be as big as 800 mm. So it is widely used in the bearing, petroleum, chemical, motors, ships and pump valve industries.
Reaction Bonded Silicon Carbide Technical Data | ||
Operating Limits | Units | SiC |
Volume Density | g/cm ³ | 3.05 |
Hardness | HV0.5 | 2000 |
Indicated Parosity | % | <0.2 |
Compressive Strength | Mpa | 2000 |
Flexural Strength | Mpa | 350 |
Free-si value | % | <12 |
Purity(SIC Percentage) | % | ≥98 |
Elastic Modulus | GPa | 350 |
Thermal Conductivity | W/m▪K | 50~100 |
Maximum Temperature | °C | 1000 |
Coefficient Of Heat Expansion(0°C~1000°C) | 10 (-6)▪1/°C | 4.0 |
Joint Power Shanghai Seals Co.,ltd was founded in 2001, located in No.333, Yuantai Road, Baoshan District,Shanghai, covering an area of 30,200 square meters with a complete production line of silicon carbide seal rings, employing 298 people. We have been specializing in production and R&D of silicon carbide seal rings for 21 years.
Main Building
Workshop
Our Products has been high recognized in more than 42 countries. We become strategic suppliers of John Crane for about 10 years.
Our products have obtained certificates of US, EU REACH, RoHS, EC1935 and UK WRAS, being widely acclaimed and recognized in 42 countries around the world. Customers' satisfaction is our greatest honor.
John Crane Best Quality Supplier Award