Product Description
EPGC308/G11 H epoxy glass cloth sheet
1. COMPOSITION AND PRESENTATION
FUWANG G11 is a stratified insulator made from fibre glass fabric and epoxy resin.
At delivery time the presentation of the sheets is as follows:
- Maximum sizes: 1020 X 2040mm / 1230X2470mm/1500X2500mm
- Colour: Nature / Light Green / Brown
- Surfaces: Shining
- Thickness: From 0.4 mm
- On demand we can deliver strips or finished components.
2. PROPERTIES.
-Very low hygrometric susceptibility.
- Small losses at high frequency.
- Excellent mechanical properties when cold.
- Good dielectric properties
- Workable while cold up to 3 mm thick
3. APPLICATIONS.
Very convenient for equipment on high frequencies and in general for all elements put under high dynamic stresses with high resistance to fatigue
4. MAIN TECHNICAL CHARACTERISTICS / SHEETS FW G11
Details data sheet for your reference:
5. http://sinofuwang.en.made-in-china.com
1. COMPOSITION AND PRESENTATION
FUWANG G11 is a stratified insulator made from fibre glass fabric and epoxy resin.
At delivery time the presentation of the sheets is as follows:
- Maximum sizes: 1020 X 2040mm / 1230X2470mm/1500X2500mm
- Colour: Nature / Light Green / Brown
- Surfaces: Shining
- Thickness: From 0.4 mm
- On demand we can deliver strips or finished components.
2. PROPERTIES.
-Very low hygrometric susceptibility.
- Small losses at high frequency.
- Excellent mechanical properties when cold.
- Good dielectric properties
- Workable while cold up to 3 mm thick
3. APPLICATIONS.
Very convenient for equipment on high frequencies and in general for all elements put under high dynamic stresses with high resistance to fatigue
4. MAIN TECHNICAL CHARACTERISTICS / SHEETS FW G11
Details data sheet for your reference:
5. http://sinofuwang.en.made-in-china.com
ITEMS | CONDITIONS | TEST METHOD | VALUES |
| Thermic endurance | in transformer oil for 4 hours | IEC 60893-2-7.1 | 180 O C ( H) |
| Specific weight | 20 O C | IEC 60893-2 | 1.80 - 2.0 g/cm 3 |
| Water absorption | 24 h | IEC 60893-2-8.2 | 1.5 mm- 19 mg |
| Flexural strength ( perpendicular ) | 23 ±2 O C | IEC 60893-2-5.1 | 340 MPa min. |
| 180 O C | 170 MPa min. | ||
| Charpy impact strength ( parallel ) | 23±2 O C | IEC 60893-2-5.4.2 | 33 KJ/m 2 min. |
| Izod impact strength ( parallel ) | 23 ±2 O C | IEC 60893-2-5.4.3 | 35 KJ/m 2 min. |
| Electric strength ( perpendicular ) | in transformer oil at 90±2 O C | IEC 60893-2-6.1 | 3.0 mm 10.2KV/mm min. |
| Breakdown voltage ( parallel ) | in transformer oil at 90 ±2 O C | IEC 60893-2-6.1 | > 3.0mm 35 KV min. |
| Insulating resistances after immersion in water | 23 ±2 O C | IEC 60893-2-6.3 | 5.0 X 10 10 min. |