Introduction
Custom 465 is a premium martensitic precipitation-hardening stainless steel that offers an excellent combination of high strength, toughness, and resistance to corrosion. The material is widely used in the aerospace, automotive, nuclear, and biomedical industries, among others, due to its superior properties. This article provides an overview of the chemical composition, mechanical properties, applications, and Anton Metal's round bar and wire rod products for medical and surgical purposes.
Precipitation-Hardening Stainless Steel Custom 465 Applications
- Aerospace: Landing gear, flap tracks, engine mounts, slat tracks, and actuators
- Medical: Surgical and dental instruments, needle wire
- Oil & Gas: Drive shafts, downhole drilling tools
- Firearms: Revolver cylinders
- Marine: Propulsion shafts
- Hand Tools: Hex keys, screwdrivers
Precipitation-Hardening Stainless Steel Custom 465 Common Trade Names
- Custom 465 (® Carpenter Technology Corporation)
- Alloy 465
- C465
- 465 Stainless
Stainless Steel Custom 465 Common Specifications
- AMS 5936 REV D
- AMS 2300 REV M
- AMS 2241 REV T
- ASTM F899 for sizes 3" Diameter and below
- ASTM A564/A5645M - 19A
- BMS 7-364 CL A REV A
- BSS 7025 (7/12/94)
- BSS 705 REV B
- SAFRAN MTL-1304
Chemical Composition
| Symbol | Element | Min % | Max % |
| C | Carbon | - | 0.02% |
| Mn | Manganese | - | 0.25% |
| Si | Silicon | - | 0.25% |
| S | Sulfur | - | 0.01% |
| P | Phosphorus | - | 0.015% |
| Cr | Chromium | 11.00% | 12.50% |
| N | Nitrogen | - | 0.01% |
| Ni | Nickel | 10.75% | 11.25% |
| Mo | Molybdenum | 0.75% | 1.25% |
| Ti | Titanium | 1.50% | 1.80% |
| Al | Aluminum | 0.90% | 1.35% |
| Fe | Iron | - | Balance |
Stainless Steel Custom 465 Mechanical Properties
| Condition | Orientation | Tensile | Yield 0.2% offset | Elongation 2" or 4D | Reduction of Area |
| H950 | Longitudinal | 240 ksi | 220 ksi | 10% | 45% ksi |
| H950 | Transverse | 240 ksi | 220 ksi | 8% | 35% ksi |
| H1000 | Longitudinal | 220 ksi | 200 ksi | 10% | 50% ksi |
| H1000 | Transverse | 220 ksi | 200 ksi | 10% | 40% ksi |
Stainless Steel Custom 465 Heat Treatment
This Material is normally supplied in Condition A (Solution Annealed)
- Heat to 1800° F ± 15° F (982° C ± 8° C), then hold at that temperature for 1 hour. Cool rapidly by quenching for parts under 12", or air cool swiftly for parts over 12"
- Refrigerate to -100° F (-73° C) and hold for eight hours, followed by warming to room temperature
- This should within a 24-hour period
- Please note that this process should be done in a 24-hour timeframe after solution annealing
Achieving high strength levels of Custom 465 requires an additional age hardening step by heating to 900 to 1150°, hold 4 to 8 hours, air cool for sizes under 3", quenching for sizes over 3".
Custom 465 Stainless Steel can be cold and hot worked with the following treatments
- Hot working: Solution anneal before hardening, then heat to 1850-2000° F (1010-1093° C) and air cool
- Cold working: Alloy 465 can be readily cold formed by drawing or rolling
Custom 465 Stainless Steel Machinability
Best machinability is in the overaged H1150M condition, but can also be done in the Solution Annealed condition.
Available Sizes And Specifications
| Custom 465 stainless steel profile sizes and specifications | |
| Grade | Custom 465 |
| Specification | EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO |
| Standard | ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 ASTM-A167 ASTM-A240 ASTM-A480. |
| Stainless steel round Bar | Diameter: 2mm - 600mm |
| Stainless steel bright Bar | Diameter: 2mm - 600mm |
| Stainless steel hex Bar | Dimension: 6mm - 80mm |
| Stainless steel square bar | Dimension: 3.0 - 180mm |
| Stainless steel flat bar | Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm |
| Stainless steel angle bar | as requirements |
| Length | Normally 6m, or produce as requirements |
| Surface | Black, Bright. Peeled and Polished, Solution annealed. |
| Delivery condition | cold drawn, hot rolled, forged, grinding, centerless grinding |
| Tolerance | H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements |