Alloy X is a nickel-chromium-iron-molybdenum alloy with an exceptional combination of high temperature strength, oxidation resistance and fabricability. It shows good ductility after prolonged exposure at temperatures up to 870ºC for 16000 hours. It also has excellent resistance to stress corrosion cracking in petrochemical applications.
CHEMICAL COMPOSITION
CHEMICAL COMPOSITION
| C | Mn | Fe | P | S | Si | Cu | Ni | Co | Al | Ti | Cr | Nb+Ta | Mo | B | N | W | La | V | Nb | |
| Hastelloy B | ≤0.05 | ≤1.0 | 4.0-6.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | ≤1.0 | 26.0-30.0 | 0.2-0.4 | |||||||||
| Hastelloy B-2 | ≤0.01 | ≤1.0 | ≤2.0 | ≤0.02 | ≤0.03 | ≤0.01 | balance | ≤1.0 | 0.04-0.07 | 26.0-30.0 | ||||||||||
| Hastelloy C | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | 50.0-58.0 | 14.5-16.5 | 15.0-17.0 | |||||||||||
| Hastelloy C-4 | ≤0.015 | ≤1.0 | ≤3.0 | ≤0.04 | ≤0.03 | ≤0.08 | balance | ≤2.0 | ≤0.7 | 14.0-18.0 | 14.0-17.0 | |||||||||
| Hastelloy C-22 | ≤0.015 | ≤0.5 | 2.0-6.0 | ≤0.02 | ≤0.35 | ≤0.08 | balance | ≤2.5 | 20.0-22.5 | 12.5-14.5 | 2.5-3.5 | 0.02 | ||||||||
| Hastelloy C-276 | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | 14.5-16.5 | 15.0-17.0 | 3.0-4.5 | ≤0.35 | ||||||||
| Hastelloy C-2000 | ≤0.01 | ≤0.5 | ≤3.0 | ≤0.025 | ≤0.01 | ≤0.08 | 1.3-1.9 | balance | ≤2.0 | ≤0.5 | 22.0-24.0 | 15.0-17.0 | ||||||||
| Hastelloy G-30 | ≤0.03 | 0.3-1.5 | 13.0-17.0 | ≤0.04 | ≤0.02 | 0.2-0.8 | 1.0-2.4 | balance | ≤5.0 | 28.0-31.5 | 4.0-6.0 | 1.5-4.0 | 0.3-1.5 | |||||||
| Hastelloy G-35 | ≤0.05 | ≤0.5 | ≤2.0 | ≤0.03 | ≤0.015 | ≤0.6 | ≤0.30 | balance | ≤1.0 | ≤0.4 | 32.25-34.25 | 7.6-9.0 | ≤0.6 | ≤0.2 | ||||||
| Hastelloy X | 0.05-0.15 | ≤1.0 | 17.0-20.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | 0.5-2.5 | 20.5-23.0 | 8.0-10.0 | 0.2-1.0 | |||||||||
| Hastelloy S | ≤0.02 | 0.3-1.0 | ≤3.0 | ≤0.02 | ≤0.015 | 0.2-0.75 | balance | ≤2.0 | 0.1-0.5 | 14.5-17.0 | 14.0-16.5 | ≤1.0 | 0.01-0.1 |
THE MINIMUM MECHANICAL PROPERTIES AT NORMAL TEMPERATURE
| Alloy and State | Tensile Strength | Yield Strength | Rate of Elongation | Brinell Hardness |
| Rm N/mm2 | RP0.2N/mm2 | A5% | HB | |
| Hastelloy B | ≥760 | ≥350 | ≥40 | - |
| Hastelloy B-2 | ≥760 | ≥350 | ≥40 | - |
| Hastelloy C | 690 | 310 | 40 | - |
| Hastelloy C-4 | ≥690 | ≥276 | ≥40 | - |
| Hastelloy C-22 | ≥690 | ≥310 | ≥45 | - |
| Hastelloy C-276 | ≥690 | ≥283 | ≥40 | - |
| Hastelloy C-2000 | ≥690 | ≥283 | ≥45 | - |
| Hastelloy G-30 | ≥586 | ≥241 | ≥30 | - |
| Hastelloy X | ≥586 | ≥241 | ≥30 | - |
| Hastelloy S | ≥110 | ≥52 | ≥46 | - |