Audited Supplier
HRARM-290
Aramid
Aramid
Aramid
The Filter Type
Filter Cartridge
Dust Filter
HEPA Filter
Pleated Cartridge
High-Temperature
Flange Mounting
HRPuri
China
Product Description
| Description | Products Code & Data |
| Aramid Filter Paper | N-ARM-290-PTFE-EI PTFE-EI : PFTE Emulsion Impregnated |
| Weight per Square Meter (Normal) | 2900 G |
| Material (Fiber/Emulsion) | ARM/PTFE |
| Thickness | 1.5~1.7 mm |
| Air permeability | 500/DM2.Min@200Pa |
| Warp Tensile Strength | > 100N/5×20cm |
| Weft Tensile Strength | > 850N/5×20cm |
| Warp Elongation | < 6%/(5×20cm) |
| Weft Elongation | < 26%/(5×20cm) |
| Continuous service Temperature | < 204ºC |
| Instant (<10Min.) Temperature bears | < 240ºC |
| Liner Shrinkage@230 ºC/2H | MD<0.3%, XD<0.3% |
| Mechanical Finish | Heat setting, singeing, calendering PTFE-ES : PFTE Emulsion Soaking |
| Chemical Finish | / |
| Mullen (PSI) | / |
| Water Repellent | / |
| Surface Electric-Resistance | / |
| Special Surface or Deep Treatment (In case client specially request to) | PTFE Membrane Laminated (PTFE-ML), or PFTE Emulsion Impregnated (PTFE-EI) |
| Other Customize Requests | Acceptable depends on MOQ. |
Increasing filter area causes the air to media ratio to decrease when the airflow stays the same. The pressure drop also decreases.