Product Description
JSA-101
JSA-101 is a two components water-based waterproof coating. Component A is consisted of high quality modified acrylic emulsion and various additives. Component B is consisted of iron-rich containing and high-alumina cement. It has the outstanding acrylic ester polymer emulsion-based performance and forms membranes with high elongation rate (above 200%), weather resistance for non-permanent immersion environment.
Where to use
Bathroom, kitchen, floors and balcony;
Waterproof layers;
Waterproof constructions under non-permanent immersion environment.
Advantages
Water-based environmental-friendly coatings;
High tensile strength with water resistance and weather resistance;
Can be applied on wet substrates with tight bonding;
Cold and convenient to apply;
Waterproofing functions with impermeableness and moisture proofing.
JSA-101 is a two components water-based waterproof coating. Component A is consisted of high quality modified acrylic emulsion and various additives. Component B is consisted of iron-rich containing and high-alumina cement. It has the outstanding acrylic ester polymer emulsion-based performance and forms membranes with high elongation rate (above 200%), weather resistance for non-permanent immersion environment.
Where to use
Bathroom, kitchen, floors and balcony;
Waterproof layers;
Waterproof constructions under non-permanent immersion environment.
Advantages
Water-based environmental-friendly coatings;
High tensile strength with water resistance and weather resistance;
Can be applied on wet substrates with tight bonding;
Cold and convenient to apply;
Waterproofing functions with impermeableness and moisture proofing.
| Item | Requirement | ||
| Solid content, % ≥ | 70 | ||
| Tensile strength, MPa ≥ | No treatment, MPa ≥ | 1.2 | |
| Retention rate after heat treatment, % ≥ | 80 | ||
| Retention rate after akali treatment, % ≥ | 60 | ||
| Retention rate after water immersion, % ≥ | 60 | ||
| Retention rate after UV treatment, % ≥ | 80 | ||
| Elongation at break, % ≥ | No treatment, MPa ≥ | 200 | |
| Heat treatment, % ≥ | 150 | ||
| Alkali treatment, % ≥ | 150 | ||
| Water immersed treatment, % ≥ | 150 | ||
| UV treatment, % ≥ | 150 | ||
| Flexibility at low temperature, ° C | -10° C, no cracks | ||
| Boding strength | No treatment, MPa ≥ | 0.5 | |
| Wet substrate, MPa ≥ | 0.5 | ||
| Alkali treatment, MPa ≥ | 0.5 | ||
| Water immersed treatment, MPa ≥ | 0.5 | ||
| Water tightness, 0.3MPa, 30min | Pass | ||