JINGBO Brand INJECTION POLYPROPYLENE HOMOPOLYMER (HP500N/HP500P)
Product Description:
Medium melt index homopolymer polypropylene resin has the advantages og high rigidity and good heat resistance deformation temperature. It's widly used in small household appliances such as electric kettles, rice cookers,hair dryers, and injection molding of household and toy priducts.
| Unit | HP500N | HP500P | ||
| Melt mass-flow rate(MFR) | g/10min | 11.6 | 18.2 | |
| Isotactic Index | % | 98.0 | 97.0 | |
| Ash content(mass fraction ) | % | 0.011 | 0.015 | |
| Yellow index | / | -2.4 | -2.8 | |
| Tensile yield stress | MPa | 34.0 | 34.5 | |
| Flexural modulus | MPa | 1561 | 1723 | |
| Charpy notched impact(23ºC) | kJ/m2 | 2.6 | 2.4 | |
| Load deformation temperature | ºC | 95 | 97 | |
| Molding shrinkage(SMp) | % | 1.2 | 1.2 | |
| Molding shrinkage(SMn) | % | 1.2 | 1.2 | |
Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.Polypropylene is a thermoplastic synthetic resin with excellent performance. It is a colorless semi-transparent thermoplastic lightweight general plastic with chemical resistance, heat resistance, electrical insulation, high strength mechanical properties and good high wear resistance. It is widely used in the production of clothing, blankets and other fiber products, medical equipment, automobiles, bicycles, spare parts, transportation pipes, chemical containers and so on. It is also used for food and medicine packaging.
| Film Grade | ||||
Item | Test condition | Test Method | Value | Unit |
| Density | ISO 1183 | 0.944-0.955 | g/cm3 | |
| MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
| Tensile strength at yield | ISO 527-2 | 22 | MPa | |
| Elongation at break | ISO 527-2 | >350 | % | |
| ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
| VICAT | ASTM D-1525 | 126 | °C | |
| Blown Grade | ||||
Item | Test Condition | Test Method | Value | Unit |
| Density | ISO 1183 | 0.950~0.955 | g/cm | |
| MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
| Tensile strength at yield | ISO 527-2 | 24 | MPa | |
| Elongation at break | ISO 527-2 | >600 | % | |
| Injection grade | ||||
Item | Test Condition | Test Method | Value | Unit |
| MFR | 190°C/2.16kg | ASTM D-1238 | 20 | g/10min |
| Density | --- | ASTM D-792 | 0.954 | g/cm3 |
| Tensile strength at yiled | --- | ASTM D-638 | 28 | MPa |
| Elongation at break | --- | ASTM D-638 | 250 | % |
| Impact tensile strength | --- | ASTM D-1822 | 42 | kJ/m2 |
| ESCR | ASTM D-1693 | 3 | --- | |
| VACIT | --- | ASTM D-1525 | 127 | °C |
1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.
2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment. And it varies according to the material and quantity.
3. About Payment Term
It's flexible, T/T, L/C at sight.
4. About the mode of transportation
(1) by sea
(2) by train
5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.