Product Description
LC8600 fast wear-resistant repair adhesive for conveying belt is a special cold patching adhesive for various conveying belts. It has the characteristics of fast solidifying at room temperature, firm adhesion with conveying belt, high tensile strength, high tear strength, high wear resistance, high impact resistance, high temperature resistance and flame resistance. It is commonly used for aging repair of working layer of strong belt (main shaft belt) in coal mines, for the rubber coating at the joint of belt buckle of conveying belt, for the anti-corrosion repair of exposed steel wire rope, for the repair of non-working layer and the working layer after tearing of the conveying belt, for the repair the sealing after the belt is excavated and repaired, for the partial-penetration repair of conveying belt, for the repair of sealing of the joint after cold vulcanization bonding of the conveying belt to prevent dust and moisture from entering into the joint, for the repair of carbonization of high-temperature conveying belt, and for the repair of the damaged and leaked outer frame of polyurethane sieve plate, etc.
Resistant to high temperature of 130°, with no flow, fast solidifying, high-bonding strength and good abrasion resistance
II. Performance
Resistant to high temperature of 130°, with no flow, fast solidifying, high-bonding strength and good abrasion resistance
II. Performance
Solidifying time ( under normal temperature), min | >10 | |
Bonding strength with conveying belt | Peel strength, Kg/cm2 | >20 |
Shear strength, Kg/cm2 | >50 | |
Tensile strength, MPa | >20 | |
Tear strength, KN/m | >70 | |
Elongation, % | >400 | |
Impact elasticity, % | 25 | |
Hardness, Shore A | 70-80 | |
Hardness, Shore A | 70-80 | |
Temperature resistance | Within 150ºC | |
Running time after belt repair | 0-10ºC,h | 2.3 |
| 10-15ºC,h | 1.8 | |
| 15-20ºC,h | 1.2 | |
| 20-35ºC,h | 0.8 | |
Repair quantity | 1.8 mm thickness | 1 square/set |