Product Description
RTV-2 Silicone Rubber Material for Stone Wall molds making
Description of RTV-2 Silicone Rubber Material for Stone Wall molds making
RTV-2 silicone rubber is a two-component material, this kind of silicone rubber consists of Part A base silicone and Part B CA30 curing agent, and Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone molds: Plaster polyurethane, PU, GRC, cement, resin, polyester, wax etc...
Features of RTV-2 Silicone Rubber Material for Stone Wall molds making
1. Good flowability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
Applications of RTV-2 Silicone Rubber Material for Stone Wall molds making
RTV2066&RTV2088 silicone rubber is especially suited for reproduction of middle size cement molds, concrete stones, and artificial stones. etc...
Storage of RTV-2 Silicone Rubber for Stone Mold Making
When the RTV-2 silicone rubber is stored at or below 30 C (85F) in the original unopened containers, Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production.
TDS of RTV-2 Silicone Rubber for Stone Mold Making
RTV2066&RTV2088 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.
| Item No. | RTV 2066 |
| Color | off-white |
| Curing agent | CA30 |
| Mixing ratio | 100:2 |
| Mixed viscosity | 25000-26000 cps |
| Pot life | 20-30 mins |
| Curing time | 2-3 Hours |
| Hardness | 28-30 Shore A |
| Tear Strength | 27 N/mm |
| Tensile Strength | ≥3.8 Mpa |
| Relative density | 1.09-1.15 g/cm3 |
| Shrinkage | ≤0.3% |
| Elongation at break | 420% |
How to make the silicone mold?
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.
Package of RTV-2 Silicone Rubber Material for Stone Wall Cladding Casting
Par A base Silicone : 5kg/pail , 20kg/pail , 25kg/pail or 200kg/pail .
Par B catalyst ( curing agent ) : 200g/bottle , 1kg/bottle , 10kg/bottle .
Certification of RTV-2 Silicone Rubber Material for Stone Wall Cladding Casting
Customer feedback :
- We are happy with MC RTV-2 silicone rubber and quality. I've also been very happy with your best service, let's continue discussions and work on more. --- Mike (from NY,USA)
- 100% love the liquid silicone rubber . I will be ordering more this week. ----Kody (from Turkey)
- We are very pleased with the quality of silicone RTV moulding rubber and the performance.------Richard from UK
- the RTV-2 silikon has arrived and is excellent------John from Iran
- I have selled some RTV molding silicone for my customer, they are very happy, so thank you-----Adam from Morroco.
Order infomation :
- MOQ: 200KG
- Delivery time:ONLY ONE DAY FOR SAMPLE CALL, 5-20 Working Days for Mass Order