Product Description
Manufactured from cross-linked polyolefin.
Provide sealing protection and strain relief over multi-core cable crutch, including 2-, 3-, 4-, and 5-core breakout.
Coated with adhesive on the body and the fingers to form a watertight seal.
Flame-retardant breakouts are available upon customer request.
Meeting with varieties of configuration requirements.
Shrink temperature:start at 90ºC,and fully recovered at 130ºC.
Provide sealing protection and strain relief over multi-core cable crutch, including 2-, 3-, 4-, and 5-core breakout.
Coated with adhesive on the body and the fingers to form a watertight seal.
Flame-retardant breakouts are available upon customer request.
Meeting with varieties of configuration requirements.
Shrink temperature:start at 90ºC,and fully recovered at 130ºC.
| Property | Test Method | Standard Value | ||
| Insulated | Oil Resistant | Semi-conductive | ||
| Breakout | Breakout | Breakou | ||
| Tensile Strength | ASTM-D-638 | ≥12MPa | ≥12MPa | ≥12MPa |
| Elongation at Break | ASTM-D-638 | ≥300% | ≥300% | ≥300% |
| (120ºC,168 hrs | ||||
| Tensile Strength | ASTM-D-638 | ≥10MPa | ≥10MPa | ≥10MPa |
| after Aging | ||||
| (120ºC,168 hrs) | ||||
| Elongation at Break | ASTM-D-638 | ≥230% | ≥230% | ≥230% |
| after Aging | ||||
| Tensile Strength | ASTM-D-638 | - | ≤20% | - |
| Variation | ||||
| after Dipping | ||||
| Elongation at Break | ASTM-D-638 | - | ≥230% | - |
| after Dipping | ||||
| Dielectric Strength | IEC 60243 | ≥15kV/mm | ≥15kV/mm | |
| Water Absorption | ISO 62 | ≤0.1% | ≤0.1% | ≤0.1% |
| Volume Resistivity | IEC 60093 | ≥1×1013Ω·cm | ≥1×1013Ω·cm | ≥1×1013Ω·cm |
| Brittle Temperature | ISO 974 | -40ºC | -40ºC | -40ºC |
| Heat Shock | 160ºC,4h | No Crack | No Crack | No Crack |
| Hardness(Shore A) | ISO 868 | ≥80 | ≥80 | ≥80 |
| Specification | Dia of Body | Dia of finger | size of conductor(mm 2 ) | usage range | color |
| ZT-2.0 | 22/12 | 11/3.5 | 10-16mm 2 | LV termination for 2 cores | black |
| ZT-2.1 | 38/19 | 15/5 | 25-50mm2 | ||
| ZT-2.2 | 58/23 | 26/8.5 | 70-120mm2 | ||
| ZT-2.3 | 88/42 | 33/14 | 150-240mm2 | ||
| ZT-3.00 | 26/20 | 11/5.4 | LV,HV termination for 3 cores | black,redmauve | |
| ZT-3.0 | 53/26 | 25/7 | 10-16mm 2 | ||
| ZT-3.1 | 73/39 | 30/10 | 25-50mm2 | ||
| ZT-3.2 | 88/48 | 38/15 | 70-120mm2 | ||
| ZT-3.3 | 108/60 | 47/18 | 150-240mm2 | ||
| ZT-3.4 | 125/70 | 65/25 | 300-500mm 2 | ||
| ZT-4.0 | 33/22 | 13/5 | 10-16mm 2 | LV termination for 4 cores | black |
| ZT-4.1 | 40/26 | 16/6 | 25-50mm2 | ||
| ZT-4.2 | 64/33 | 26/7.5 | 70-120mm2 | ||
| ZT-4.3 | 76/42 | 33/11 | 150-240mm2 | ||
| ZT-5.0 | 35/21 | 13/5 | 10-16mm 2 | LV termination for 5 cores | black |
| ZT-5.1 | 52/29 | 16/5 | 25-50mm2 | ||
| ZT-5.2 | 80/39 | 26/10 | 70-120mm2 | ||
| ZT-5.3 | 93/46 | 33/11 | 150-240mm2 |