Product Description
anticorrosive and moisture-proof coating
Descriptions:
J55 type anticorrosive coating is composed of modified chlorosulfonated polyethylene, epoxy, and a variety of polymer synthetic resin, nano beads, additives and other organic and inorganic materials polymerized anticorrosive coating, the product has the characteristics of non-toxic, non-polluting, can be applied in the wet surface.
It is the most ideal coating material for cooling tower of power plant.
Used areas:
Waterproof and anticorrosive concrete structures, pools, sewage ponds, sluice gates, DAMS, Bridges, tunnels, viaducts, wharves, old and new cooling towers and other structures.
Technical data:
Notes:
Clean the surface of concrete, firm and dense, do not show the bar, sand, dust, empty shell, crack, pitted surface and other defects.
The total thickness of the dry film is >120UM. After coating, the film is smooth and smooth without any bulging, bubbling or falling off. It can be put into use only if the curing period is ≥ 15 days (23 degrees Celsius).
This product is a kind of coating with one bottom and one surface. It is strictly prohibited to mix solvents or other media into the coating.
Paint construction, storage temperature is > 5 degrees Celsius, strong wind, heavy rain bad weather can not be construction, shelf life of 1 year.
Descriptions:
J55 type anticorrosive coating is composed of modified chlorosulfonated polyethylene, epoxy, and a variety of polymer synthetic resin, nano beads, additives and other organic and inorganic materials polymerized anticorrosive coating, the product has the characteristics of non-toxic, non-polluting, can be applied in the wet surface.
It is the most ideal coating material for cooling tower of power plant.
Used areas:
Waterproof and anticorrosive concrete structures, pools, sewage ponds, sluice gates, DAMS, Bridges, tunnels, viaducts, wharves, old and new cooling towers and other structures.
Technical data:
| NO | performance | Technical indicators |
| 1 | Dry time(h) | Surface dry≤2h real dry 4 h |
| 2 | Bond strength | ≥0.5MPA |
| 3 | Impact strength/cm | >40 |
| 4 | wash resistance | >2000times |
| 5 | Adhesion(Row lattice method)% | 100 |
| 6 | Flexibility(mm)≤ | 1 |
| 7 | Resistance to chemical medium, 3% H2SO4, solution 96h, 10% NaOH solution 96 h ,and 10%NaCL solution 96h | The film does not change and does not come off |
Notes:
Clean the surface of concrete, firm and dense, do not show the bar, sand, dust, empty shell, crack, pitted surface and other defects.
The total thickness of the dry film is >120UM. After coating, the film is smooth and smooth without any bulging, bubbling or falling off. It can be put into use only if the curing period is ≥ 15 days (23 degrees Celsius).
This product is a kind of coating with one bottom and one surface. It is strictly prohibited to mix solvents or other media into the coating.
Paint construction, storage temperature is > 5 degrees Celsius, strong wind, heavy rain bad weather can not be construction, shelf life of 1 year.