UL94 V2 Certified Eco-Friendly Flame Retardant Additive for Copoly PP, Homo-PP
Introduction:
Mflam AMH-01S is a flame retardant especially designed for polyolefin, with phosphorus,bromine and nitrogen as the main flame retardant elements.
It has high flame retardant efficiency, add 0.5% in homopolymer PP and add 2% in co-polymer PP, to achieve UL94 V2.
Good thermal stability, no immigration, excellent water resistance, good agingresistance and low smoke non-toxicity, no heavy metal, will not influence the transparent color of PP.
Specification:
| Item | Index |
| Appearance | White Powder |
| The Content of Phosphorus %(W/W) | 16±2 |
| The Content of Nitrogen %(W/W) | 22±2 |
| Bromine content % | 7±2 |
| Particle Size D50 (μm) D90 (μm) | 9±4 20±5 |
| Moisture %(W/W) | ≤0.5 |
| Process condition ºC | ≤210 |
Package Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 20mt with pallet in 1x 20'FCL
Recommended dosage:
| Resin | Homo poly PP | Copoly PP | Homo PP+20% talcum powder | Copoly PP+Homo poly PP +10% talcum powder |
| Dosage % Mflam AMH-01S | ≥0.5 | ≥2 | ≥1 | ≥3 |
| UL94 | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) |
Remarks:
1) The process temperature of Mflam AMH-01 S is recommended under 230 °C,so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
2) When add Mflam AMH-01 S in PP, it is not suggested to use Strong shear screw.