PROCESSING AID ZB-125 ZB130 ZB140 ZB150
Brief Introduction
They are processing aid made from acrylate monomer by emulsion polymerization.
The products are mainly used to improve process property,promote fusion,reduce process temperature.
Improve the surface quality of the finished product.
The products are amorphous white powder,They can be dissolved in kotone and chloroform,but not in water and alcohol.
The sanitary index is accordance with GB9681-88.
Quality Specificati
Property and Application
Brief Introduction
They are processing aid made from acrylate monomer by emulsion polymerization.
The products are mainly used to improve process property,promote fusion,reduce process temperature.
Improve the surface quality of the finished product.
The products are amorphous white powder,They can be dissolved in kotone and chloroform,but not in water and alcohol.
The sanitary index is accordance with GB9681-88.
Quality Specificati
| ITEM | ZB-125 | ZB-130 | ZB-140 | ZB-150 |
| Inherent Viscosity [η]25ºC | 4.5-605 | 8.0-10.0 | 3.0-4.0 | 11-12 |
| Bulk Density,g/cm3≥ | 0.35 | 0.35 | 0.35 | 0.35 |
| Volatile matter,%≤ | 1.5 | 1.5 | 1.5 | 1.5 |
| Particle Size[0.45mm(40mesh)passed]%≥ | 98 | 98 | 98 | 98 |
Property and Application
| ITEM | ZB125 | ZB130 | ZB140 | ZB150 |
| Main Application | To be used in window, window profile,sheet,pipe fitting,etc | To be used in window, window profile,sheet,pipe fitting,etc | To be used in window, window profile,sheet,pipe fitting,etc | To be used in window, window profile,sheet,pipe fitting,etc |
| Typical Characterstic | good fluidity,it is fit for opaque product. | good comprehensive property and good fusion property | good comprehensive property and good fusion property | good comprehensive property and good fusion property |
| Improve Fusion | * * * * | * * * * * | * * * * * | * * * * |
| Enhance Melt Strength | * * * * | * * * | * * * | * * * * * |
| Melt Viscosity | * * * | * * * * * | * * * * * | * * * * |
| Transparency | * * * | * * * * | * * * * * | * * * |
| Dispersancy | * * * * * | * * * * | * * * * | * * * |