M33 Molybdenum High Speed Tool Steel (UNS T11333)
| Price | $3000.00 |
|---|---|
| Min Order | 1 Ton |
| Availability | In Stock |
| Shipping From | Hunan, China |
| Popularity | 465 people viewed |
Model NO.:
M33
Type:
Alloy Steel Bar
Standard:
ASTM
Composition:
Ferrous Steel Scrap
Technique:
Hot Rolled, Forged
Shape:
Round, Square, Flat
Surface Treatment:
Black, Grinded, Peeled, Polished, Rough Turned
Special Use:
Wear Resistant Steel
Application:
Structural Steel Bar
Similar Grades:
T11333
Size Range:
Diameter: 20-480mm
Delivery Condition:
Annealed, Qunched and Tempered
Surface Condition:
Black, Grinded, Peeled, Polished, Rough Turned
Quality Standard:
ASTM -A600
Trademark:
FUSHUN
Transport Package:
Apply The Shipping Packing
Specification:
Diameter: 20-480mm
Origin:
Hubei, Huangshi
HS Code:
7228600000
Product Description
Similar Grades:
T11333
Shape:
Round, Flat, Square.
Size Range:
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
Chemical Composition(%)
Fabrication and Heat Treatment
Forming
Conventional methods are used for forming of M33 molybdenum high speed tool steel.
Welding
M33 molybdenum high speed tool steel is weldable.
Machinability
M33 tool steel has medium machinability that is rated at 55% to 60%.
Forging
M33 tool steel is forged at 1121°C (2049°F) down to 954°C (1749°F). It has been recommended that forging below 927°C (1700°F) should not be carried out for M33 tool steel.
Heat Treatment
M33 tool steel is preheated to 787.8 °C (1450°F) and rapidly heated to 1204-1232°C (2199-2249°F). It is then held for 2 to 5 minutes. Salt bath, air quenching or oil can be used for heat treatment of M33 tool steel.
Annealing
Annealing for M33 tool steel takes place at 885°C (1625°F) and this is followed by cooling the steel slowly in a furnace at less than 4°C for an hour.
Cold Working
Conventional methods are followed for cold working of M33 tool steel.
Tempering
M33 too steel is tempered at 538 °C to 593°C (1000.4°F - 1099.4°F) for Rockwell C of 65 to 60. The tempering process is repeated to obtain better results.
Hardening
Tempering and heat treatment process details are applied for the hardening of M33 tool steel.
Hot Working
This process is carried out by consulting the supplier for lower temperature working information besides referring to the forging data.
Applications
M33 molybdenum high speed tool steel is used for all varieties of cutting tools.
T11333
Shape:
Round, Flat, Square.
Size Range:
| Diameter(mm) | Thickness (mm) | Width (mm) | Length(mm) | |
| Round | 20-480 | - | - | 2000-5800 |
| Square | 20-480 | - | - | 2000-5800 |
| flat | - | 20-50 | 80-600 | 2000-5800 |
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details | In seaworthy packing, as your requirement. |
| Delivery details | within 30-50 days |
| C | Si | Mn | P | S | Cr | Mo | V | W | Co |
| 0.85-0.92 | 0.15-0.50 | 0.15-0.40 | 0.03max | 0.03max | 3.50-4.00 | 9.00-10.00 | 1.00-1.35 | 1.30-2.10 | 7.75-8.75 |
Fabrication and Heat Treatment
Forming
Conventional methods are used for forming of M33 molybdenum high speed tool steel.
Welding
M33 molybdenum high speed tool steel is weldable.
Machinability
M33 tool steel has medium machinability that is rated at 55% to 60%.
Forging
M33 tool steel is forged at 1121°C (2049°F) down to 954°C (1749°F). It has been recommended that forging below 927°C (1700°F) should not be carried out for M33 tool steel.
Heat Treatment
M33 tool steel is preheated to 787.8 °C (1450°F) and rapidly heated to 1204-1232°C (2199-2249°F). It is then held for 2 to 5 minutes. Salt bath, air quenching or oil can be used for heat treatment of M33 tool steel.
Annealing
Annealing for M33 tool steel takes place at 885°C (1625°F) and this is followed by cooling the steel slowly in a furnace at less than 4°C for an hour.
Cold Working
Conventional methods are followed for cold working of M33 tool steel.
Tempering
M33 too steel is tempered at 538 °C to 593°C (1000.4°F - 1099.4°F) for Rockwell C of 65 to 60. The tempering process is repeated to obtain better results.
Hardening
Tempering and heat treatment process details are applied for the hardening of M33 tool steel.
Hot Working
This process is carried out by consulting the supplier for lower temperature working information besides referring to the forging data.
Applications
M33 molybdenum high speed tool steel is used for all varieties of cutting tools.