Manufacturer Stainless Steel Welding Electrode Welding Rod Aws E309-16
| Price | $4.70 |
|---|---|
| Min Order | 1000 kg |
| Availability | In Stock |
| Shipping From | Hebei, China |
| Popularity | 278 people viewed |
Model NO.:
E309-16
Type:
H (Heat Resistant Low Alloy Steel/ Stainless Steel Electrode)
Material:
Stainless Steel
Diameter:
2.0~5.0mm
Length:
300-400mm
Welding Core Type:
Stainless Steel
Electrode Coating Type:
Titanium Calcium
Slag Characteristic:
Acidic
Stainless Steel Welding Rod Type:
Chromium Stainless Steel
Function:
Low Hydrogen Type Electrode, Gravity Electrode, Moisture-Proof Electrode
Welding Power:
DC/AC
Trademark:
JINYUAN
Transport Package:
Customized
Specification:
3.2x350mm 2.5x300mm 4.0/5.0x400
Origin:
China
HS Code:
8311100000
Product Description
The whole is made of high-quality steel, which is not easy to rust, has a smooth surface and a long service life.
Professional production technology, stable structure, attention to every detail.
Professional production technology, stable structure, attention to every detail.
Use professional testing equipment to strictly test products to ensure product quality.
Basic Info.
| Model NO. | E308-16, E308L-16, E309-16, E309L-16,E312-16,E316L-16 |
| Length | 300-400mm |
| Electrode Coating Type | Titanium Calcium |
| Welding Power | AC/DC |
| Origin | China |
| Diameter | 2.0~5.0mm |
| Welding Core Type | Stainless Steel |
| Transport Package | Carton |
| Function | For welding of the working temperature is less than 300 ºC corrosion resistant stainless steel structure, such as SUS304 etc.. |
| Trademark | JINYUAN |
Product Specification
| E309-16 | |||||||||
| Chemical Composition Of Deposited Metal (%) | |||||||||
items | C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
Requirements | ≤0.15 | 0.5-2.50 | ≤1.00 | 22.0-25.0 | 12.0-14.0 | ≤0.75 | ≤0.75 | ≤0.03 | ≤0.04 |
Typical Results | 0.06 | 0.89 | 0.69 | 24.05 | 12.5 | 0.10 | 0.08 | 0.010 | 0.028 |
| Mechanical Properties of Deposited Metal (AW) | ||
items | Tensile Strength Rm (MPa) | Elongation A4(%) |
Requirements | ≥550 | ≥25 |
Typical Results | 600 | 38 |
| E308-16 | |||||||||
| Chemical Composition Of Deposited Metal (%) | |||||||||
| items | C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
| Requirements | ≤0.08 | 0.5-2.5 | ≤1.00 | 18.0-21.0 | 9.0-11.0 | ≤0.75 | ≤0.75 | ≤0.03 | ≤0.04 |
Typical Results | 0.06 | 0.87 | 0.67 | 20.00 | 9.50 | 0.09 | 0.08 | 0.010 | 0.025 |
| Mechanical Properties of Deposited Metal (AW) | ||
| items | Tensile Strength Rm (MPa) | Elongation A4(%) |
| Requirements | ≥550 | ≥30 |
Typical Results | 596 | 43 |
| E308L-16 | |||||||||
| Chemical Composition Of Deposited Metal (%) | |||||||||
| items | C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
| Requirements | ≤0.04 | 0.5-2.50 | ≤1.00 | 18.0-21.0 | 9.0-11.0 | ≤0.75 | ≤0.15 | ≤0.03 | ≤0.04 |
| Typical Results | 0.029 | 0.86 | 0.63 | 19.80 | 9.60 | 0.10 | 0.022 | 0.012 | 0.024 |
| Mechanical Properties of Deposited Metal (AW) | ||
| items | Tensile Strength Rm(Mpa) | Elongation A4(%) |
| Requirements | ≥520 | ≥35 |
Typical Results | 575 | 46 |
| E309L-16 | |||||||||
| Chemical Composition Of Deposited Metal (%) | |||||||||
items | C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
Requirements | ≤0.15 | 0.5-2.50 | ≤1.00 | 28.0-32.0 | 8-10.5 | ≤0.75 | ≤0.75 | ≤0.03 | ≤0.04 |
Typical Results | 0.085 | 1.11 | 0.78 | 29.39 | 9.97 | 0.16 | 0.2 | 0.011 | 0.028 |
| Mechanical Properties of Deposited Metal (AW) | ||
items | Tensile Strength Rm (MPa) | Elongation A4(%) |
Requirements | ≥510 | ≥25 |
Typical Results | 565 | 41 |
| E312-16 | |||||||||
| Chemical Composition Of Deposited Metal (%) | |||||||||
items | C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
Requirements | ≤0.15 | 0.5-2.50 | ≤1.00 | 28.0-32.0 | 8-10.5 | ≤0.75 | ≤0.75 | ≤0.03 | ≤0.04 |
Typical Results | 0.085 | 1.11 | 0.78 | 29.39 | 9.97 | 0.16 | 0.2 | 0.011 | 0.028 |
| Mechanical Properties of Deposited Metal (AW) | ||
items | Tensile Strength Rm (MPa) | Elongation A4(%) |
Requirements | ≥660 | ≥15 |
Typical Results | 785 | 26 |
| E316L-16 | |||||||||
items | C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
Requirements | ≤0.04 | 0.5-2.50 | ≤1.00 | 17.0-20.0 | 11-14 | 2-3 | ≤0.75 | ≤0.03 | ≤0.04 |
Typical Results | 0.030 | 1.01 | 0.68 | 19.01 | 11.82 | 2.46 | 0.08 | 0.015 | 0.025 |
| Mechanical Properties of Deposited Metal (AW) | ||
items | Tensile Strength Rm (MPa) | Elongation A4(%) |
Requirements | ≥490 | ≥25 |
Typical Results | 580 | 45 |
Attention:
1.The electrode must be re-dry by 320ºC-350ºC for 1 hour before welding,2.The rust, oil, water and other impurities of the weld area must be removed before welding.
3.DC*is better than AC, lower heat input is suggested, the temperature of preheat and interpass keep under 150ºC
Packing Details
Certification:
- Similar Products
Negotiable
5000 kg (MOQ)
Stick Electrodes Aws: E7018 Good Quality
Hangzhou Linan Dayang Welding Material Co., Ltd.
$0.78
1000 kg (MOQ)
Enife-Ci Ni99 Cast Iron Welding Electrode Rod Good Quality
Qingdao Superweld Co., Ltd