Strong Resistant to Heat Checking Ymt2367r Mold Steel
| Price | $5.50 |
|---|---|
| Min Order | 10 kg |
| Availability | In Stock |
| Shipping From | Jiangsu, China |
| Popularity | 355 people viewed |
Model NO.:
YMT2367R
Type:
Steel Plate
Standard:
AISI, DIN, JIS, GB
Composition:
C: 0.32-0.40 Si:0.30-0.40 Mn:0.30-0.50 V:0.40-0.70
Technique:
Forged
Shape:
Block
Surface Treatment:
Black Primer
Special Use:
High-strength Steel Plate, Wear Resistant Steel, Mold Steel
Application:
Tool Steel Bar
Usage:
Aluminum, Zinc, Die Casting and Plastic Mold
Trademark:
YMT
Transport Package:
Container or Metal Framework
Specification:
Max 500mm thickness
Origin:
China
HS Code:
7224909090
Product Description
YMT2367ESR
YMT2367ESR hot work tool steel has high temperature strength and good wear resistance in high temperature environment, and twice hardened steel has good tempering, high through hardening and toughness, can be used directly during production in cooling water
Chemical Composition :
| Steel grade (%) | C | Si | Mn | Cr | Mo | V |
| YMT 2367ESR | ~0.38 | ~0.40 | ~0.40 | ~5.00 | ~2.5 | ~0.60 |
Main Applications
It is for the production of wear-resistant tools, warm extrusion compression dies, and light and heavy metal forging dies and other hot work tools and accessories. Specially for the higher requirements of working environment, we recommend the use of electroslag remelting steel YMT2367ESR.
Physical Property
Density[g/cm3]:
| 20OC 7.83 |
Thermal Conductivity [W/m.K]:
| 20OC 25 |
Coefficient of Linear Thermal Expansion 10-6°C-1
| 20-100 °C | 20-200 °C | 20-300 °C | 20-400 °C | 20-500 °C | 20-600 °C | 20-700 °C |
| 11.5 | 12.0 | 12.2 | 12.5 | 12.9 | 13.0 | 13.2 |
Non-metallic Inclusion
As per ASTM E45 method A
At ≤1.5, Bt≤l.5, Ct≤l.5, Dt≤l.5; Ad≤1,5, Bd≤l.5, Cd≤1.5, Dd≤l.5 or DIN50602-K4≤20 or subject to customer's requirements.
UT Test Standard
SEP 1921 Group3, Class E/e or subject to customer's requirements.
Delivery Conditions
Delivered in pre-hardened condition, max hardness 235HB, or according to customer's requirement.
Heat-Treatment
Air cooling, oil quenching or 450-550OC salt bath. App. HRC50-56
| Soft annealing temperature | Quenching temperature |
| 800-840OC | 1030-1080OC. Air cool, oil cool or hot bath (500-550OC, Quenching hardness 53-57HRC. |
Stress Relieving
Heat to 650OC, keep in furnace for one hour, then air cooling in order to alleviate stress during machining
Or reduce the deformation caused in the heat treatment.
Tempering and Hardness, UTS
| Tempering temperature [ o C] | 100 | 200 | 300 | 400 | 500 | 550 | 600 | 650 | 700 |
| HRC | 57 | 55 | 54 | 53 | 56 | 56 | 53 | 43 | 31 |
| UTS ([N/mm2 ] | 2140 | 1980 | 1910 | 1845 | 2010 | 2050 | 1845 | 1360 | 995 |
- Similar Products
$2200.00
1 Ton (MOQ)
SKD11 X165crmov12 1.2601 D2 Mold Steel Plate
Wuxi Taixie Metal Material Co., Ltd.
$9.80
1 Square Meter (MOQ)
Weather Resistant Coil for Premium Quality Aluminum Roofing Support
Kexinda(Tianjin)Industrial Co., Ltd