1J46 46Ni-Fe Softe Magnetic Alloy Equivalent to PERMENORM5000 H2 High Permability45 PB-1
Transformer Grade PERMENORM 5000 H2 exhibits a very coarse-grained, anisotropic structure after final heat treatment. The cold rolled material can show a cubic texture which results in high permeability values in the rolling direction and to some extent in transverse direction after the final annealing.
PERMENORM 5000 exhibits the highest saturation polarization of 1.55 T in the NiFe system in combination with a high initial and maximum permeability.
PERMENORM 5000 H2(1J46) is available as solid material (bar, rod, wire) or as cold rolled strip in thicknesses from 0.025 mm to 2.0 mm. PERMENORM 5000 V5 is available as cold rolled strip in thicknesses from 0.05 mm to 2.0 mm.
For optimum magnetic properties PERMENORM 5000 should be annealed in an oxygen-free, dry hydrogen atmosphere with a dew point below -40°C, at a temperature above 1000°C. Recommended parameters for stationary annealing are 5 h 1150°C.
Chemical Composition(%)
| Name | Ni | Fe | Other |
1J46 46Ni-Fe (Permenorm 500 H2) | 46-47.5 | Balance | Mn,Si |
Magnetic Properties (dynamic (50Hz) properties of solid material, measured on stamped rings)
| Material | Permeabilityμ @ 0.4 A/m | Permeability μmax | Lossse@1T | Saturation polarization |
1J46 46Ni-Fe (Permenorm 500 H2) | 12000 | 90000 | p=0.25W/KG at thickness 0.2mm | 1.55T |
Physical properties
| Mass density | 8.25 g/cm³ |
| Electrical resistivity | 0.45 Ohm mm²/ m |
| Thermal conductivity | 13 - 14 W/m/K |
| Curie temperature | 440°C |
| Coefficent of Thermal Expansion (20..200°C) | 8.85 · 10-6/K(after final magnetic annealing) |
Mechanical properties
| Tensile strength | 850 - 1100 N/mm² |
| Young´s modulus | 195 kN/mm² |
| Vickers hardness HV | 220 - 300 |
1J46 46Ni-Fe (Permenorm 500 H2) Application
1.Inductive Components and Cores 2.Strip Wound Cores 3.Relay Parts 
4.Measurement Transducers 5.Rotor and Stator Laminations
6.Flux Conductors 7.Pole Pieces in Magnetic Valves