MadeInChina.com > Auto & Motorcycle Parts > Auto Parts > Brake

59/72/75 Teeth Laminated Gear Clutch Facing for Engineering Machinery

Price	$80.00 Compare
Min Order	5 Pieces
Availability	In Stock
Shipping From	Guizhou, China
Popularity	220 people viewed
Quantity	+-

Guiyang Talent Friction Material Co., Ltd.

Audited Supplier 7 years

Profile Certified by SGS/BV

Guizhou, China
huang (Ms.)

Visit Homepage Product Catalog

Product Detail
Contact Supplier

Model NO.:

TL3000

Type:

Gear Teeth Ring

Material:

Non-Asbestos

Position:

Industrial Clutch

Certification:

ISO/TS16949

Classification:

Gear Teeth Ring

Drum Brakes Classification:

Gear Teeth Ring

Main Market:

North America, Africa

Application:

Oil Drilling Machinery

Application2:

Industrial Brake Clutch

Application3:

Desch Clutch Brake

Application4:

Wpt Clutch Brake

Color:

Yellow

Teeth:

59/72/75/87/63 Teeth

Measurement:

10"/11"/14"/18"/21 Inch

Trademark:

TALFRI

Transport Package:

Pallet

Specification:

as required

Origin:

China

HS Code:

8483900090

Product Description

TL3000, Non Asbestos Gear Teeth Facing For Industrial Brake/ Clutch System, is a Non Asbestos Woven Laminated Sheet with exceedingly high hardness and strength. The material is woven from Kevlar and other synthetic fabric yarns containing brass wire. After being impregnated with special resin and pressed into rigid flat sheet, the material shows outstandingly good resistance to wear and compression and excellent stability.
TL3000 is a heavy duty material extensively used in oil drilling and wind power industry. It can be installed in industrial brake and clutch system, power transmission system and electric magnetic brake engine.

Dimension:
Length x Width:762mm x 762mm (30 inches x 30 inches)
Thickness:3.2mm-12.7mm ( 1/8 - 1/2 inch)

Frictional Properties:
Normal 0.48
Hot 0.42
Static, 200°F 0.50
Static, 400°F 0.48

Recommended Operating Range:
Max. Pressure, psi 250
Max. Rubbing Speed, ft/min 5000
Max. Intermittent Temperature 600°F (315°C)
Max. Continuous Temperature 550°F (287°C)