Product Description
| Type | Rolling Wire |
| Material | 500MPa grade carbon steel wire |
| Flux Containing | Not Containing Flux |
| Extended Length: | >20mm |
| Shielding Gas | CO2 |
| Sep | 0.8, 1.0, 1.2,1.6 |
| Rm/MPa | 490-670 |
| ReL/Rp0.2MPa | >=420 |
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=420 | >=20 |
| example value | 560 | 450 | 26 |
Versatile Applications: Expertly engineered for welding carbon steel and low alloy steel structures of corresponding strength levels, our product shines in construction machinery, shipbuilding, vehicle manufacturing, and the petrochemical industry.
Distinctive Features: The HH-50S-6 wire, crafted for 500MPa level carbon steel, employs CO2 gas-shielded welding to minimize spatter. It delivers beautiful shaping, high deposition efficiency, and excellent all-position welding capabilities with reduced porosity sensitivity of the weld metal.
Molten Metal Mechanical Properties (CO2):
| sports event | C | Mu | Si | S | P | Ni | Cr | Mo | V | Cu |
| standard value | 0.06-0.15 | 1.40-1.85 | 0.80-1.15 | <=0.025 | <=0.025 | <=0.15 | <=0.15 | <=0.15 | <=0.03 | <=0.50 |
| example value | 0.08 | 1.50 | 0.89 | 0.012 | 0.013 | 0.03 | 0.02 | 0.002 | 0.003 | 0.11 |
1. Ensure the removal of rust, oil, water, and other impurities from the weldment surface for optimal welding results.
2. The welding wire energy level is crucial for the weld's mechanical properties. For structures of significant importance, prioritize using smaller wire energy to maximize strength and integrity.