HH-CE71T-1
Rolling Wire
Stainless Steel
Not Containing Flux
Acidic
10-20mm
Accepted
Negotiable; Around 30-35 Days
ISO 9001; CE; RoHS; Reach; OHSAS
200000 Tons
Honglu
as Per Request
0.8; 1.0; 1.2; 1.6
Anhui, China
7505220000
Product Description
Uses: Ideal for industries such as shipbuilding, bridge construction, marine engineering, and steel structural projects, offering robust and reliable welding solutions.
Characteristics: Our HH-CE71T-1 represents the pinnacle of CO2 gas-shielded flux-cored wires with a rutile slag system. It is engineered for versatility, allowing welding in any position with unparalleled ease. Its outstanding process performance ensures a stable arc and effortless slag removal, coupled with impressive low-temperature impact properties.
Chemical composition of welding wire: (mass fraction) 100%
| sports event | C | Mn | Si | S | P | Ni | Cr | Mo | V |
| standard value | <=0.18 | <=2.00 | <=0.09 | <=0.030 | <=0.030 | <=0.50 | <=0.20 | <=0.30 | <=0.08 |
| example value | 0.055 | 1.43 | 0.2 | 0.017 | 0.012 | 0.11 | 0.04 | 0.028 | 0.016 |
Mechanical properties of molten metal: (CO2)
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=390 | >=18 |
| example value | 564 | 460 | 24 |
Precautions:
1, Engage in CO2 gas shielded welding with a gas purity of no less than 99.98% to ensure optimal results.
2, Maintain the CO2 shielding gas flow at an optimal 18-25L/min. 3, Ensure the welding wire's protrusion length is consistently within 15-25mm for best performance.