Audited Supplier
Micro Fiber
Concrete Reinforcement
White
6-18mm,Custom Length
High-strength Polypropylene Fiber
High Tenacity
Microfiber
160-170
>5.0gpa/3.0gpa
>500MPa/350MPa
15-30%/50%
HongLi
Carton Packing
3/4/6/8/12/16/18/Custom Length
Shandong, China
7217301000
Product Description
Product description
The polypropylene fiber produced by our company is a synthetic fiber made by adding 100% modified polypropylene into the masterbatch, blending, spinning, stretching, antistatic and ultraviolet resistance. It is a special fiber of concrete and mortar, which can effectively control the cracks of concrete and mortar caused by shrinkage, shrinkage and temperature change. Amine is non-toxic, acid and alkali resistant, antimagnetic and antirust, and has strong binding force with cement. It greatly improves the crack resistance, impermeability and erosion resistance, and increases the toughness of the concrete, thus prolonging the service life.
Application area
1. Anti-crack, anti-seepage and thermal insulation mortar for industrial and civil buildings.
2. Concrete pouring projects with high impermeability and impact resistance such as working face dam, spillway and diversion hole in water conservancy and hydropower projects.
3. Various precast concrete products.
4. Concrete for roads, bridges, tunnels and airport runways.
5. Chemical plants with high requirements for alkali resistance and chemical corrosion.
| Product Name | Model | Materials | Shape | Density | Melting Point | Equivalent Diameter | Tensile Strength | Elastic Modulus | Elongation at Break | Length(mm) |
| High Strength | HLBG | Modified polypropylene | Monofilament Bundle | 0.91g/cm3 | 160-170 | 20-50um | >500Mpa | >5.0Gpa | 15-30% | 3/4/6/8/12/16/18 custom length |
| Hollow type | HLBK | Modified polypropylene | Monofilament Bundle | 0.91g/cm3 | 160-170 | 70-100um | 350Mpa | 3.0Gpa | 50% | 3/4/6/8/12/16/18 custom length |