Audited Supplier
YN-0006
Refractory, Industrial Ceramics
1-10um
95%
Ceramic Part
Punch Forming
Unidirectional Pressurization
Ivory, Cream, White, Pink Color
Arc, Conical, Cylinderical, Tubular, Tall Form
High Temperature and Chemical Corrosion
Sintering and Melting of Glass, Phosphors
for Chemical Calcining, Metal Casting, and Ceramic
1600c, 1700c, 1800c
Yunnuo
Carton
CUSTOMIZED
China Shanghai
8547100000
Product Description
Textile ceramics are mainly produced from alumina ceramic materials, which have excellent comprehensive technical properties such as high mechanical strength, high hardness, low high-frequency dielectric loss, high temperature insulation resistance, chemical resistance and good thermal conductivity.
Material option:
Steatite
Alumina up to 99.7 % or 95% alumina
Titania
Zirconia
Range of products:
Flange Eyelet, Double flange eyelet, Slotted eyelet, groove eyelets, step eyelet, Cut Eyelet, Step Eyelets, Tubes, Rods, Sleeve,
Ring, Bush, Disc, Dish, Washer, Plates Trap Guide, Traverse Guide, Pig tail Guide, Dog tail Guide, Rollers, Oilers, Oiling Nozzles Cutters
Application :
Yarn manufacturing machines
Twister machines
Airjet looms
Circular looms
weaving machines
winder machines
Rope,Tap plants
Customized guides as per detailed drawings and specifications.
Item | Unit | 95% al2o3 | 99% al2o3 | Zirconia | Black Tio2 | Yellow Tio2 |
Color | white,pink | cream,pink | white,black,yellow | Black | Yellow | |
Density | g/cm3 | 3.65 | 3.9 | 6 | 4 | 4 |
Flexural strength | MPA | 290 | 390 | 1300 | 70 | 70 |
Compressive strength | MPA | 3300 | 3900 | 3000 | 600 | 600 |
Vickers hardness | HV0.5 | 1800 | 2000 | 1150 | 900 | 900 |
Thermal expansion cofficient | 10-6 K-3 | 5-8.3 | 5.4-8.3 | 10 | 8.5 | 8.5 |
Thermal conductivity | w/mk | 23 | 28 | 2 | 25 | 25 |