Audited Supplier
AWS E6013, AWS E7018
E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
Cast Iron
3.2mm
300mm, 350mm, 400mm
Carbon Structural Steel
Titanium
AC&DC
Aws E6013
Black, Red, Green, Blue, Grey
2.0mm, 2.5mm, 3.2mm, 4.0mm, 5.0mm
8 10 12 14
2.5/5kgs/Inner Box, 20kga/Outer Box
Great Wall
ISO 9001, ABS, CE, Aws, CQC
GREAT WALL
2.5/5kgs/Inner Box and 20kgs/Outer Box
2.5X300MM, 3.2X350MM, 4.0X400MM, 5.0X400MM
Hebei China
83111000
Product Description
E7018 E6013 E6011 WELDING ELECTRODES & RODS
1. Size 2.5 3.2 4.0 5.0mm
2. 5kg/box 20kg/carton
3. Samples free
4. OEM accept
E7018 E6013 E7016 E6011 E6010 WELDING ELECTRODES
CARBON STEEL WELDING ELECTRODE /MS welding electrode
Certificate: ISO CE AWS SONCAP CIQ COC BV ABS DNV LR GL
DIA: 2.5mm*300/350mm 3.2mm*350mm 4.0mm*400mm 5.0mm*400mm
Application:
Suitable for welding sheet metal structuremade of low-carbon steel, such as ships, vehicles, building, and general machinery.
Product Superiority
1) Good antipore performance: As long as the electrode is not affected with with damp, ordried at 250~3000C before using, pores cannot appear
2) While welding operation, electrode manipulation is freely, hand felling is comfortable with little spatter and the welding slagis easy to flake(Normally it flakes automaticall while downhandweldingandanglewelding). The forming of welding seam is formed beautifully.
Mechanical Properties of Deposited Metal:
Recommended Welding Current:
1. Size 2.5 3.2 4.0 5.0mm
2. 5kg/box 20kg/carton
3. Samples free
4. OEM accept
E7018 E6013 E7016 E6011 E6010 WELDING ELECTRODES
CARBON STEEL WELDING ELECTRODE /MS welding electrode
Certificate: ISO CE AWS SONCAP CIQ COC BV ABS DNV LR GL
DIA: 2.5mm*300/350mm 3.2mm*350mm 4.0mm*400mm 5.0mm*400mm
Application:
Suitable for welding sheet metal structuremade of low-carbon steel, such as ships, vehicles, building, and general machinery.
Product Superiority
1) Good antipore performance: As long as the electrode is not affected with with damp, ordried at 250~3000C before using, pores cannot appear
2) While welding operation, electrode manipulation is freely, hand felling is comfortable with little spatter and the welding slagis easy to flake(Normally it flakes automaticall while downhandweldingandanglewelding). The forming of welding seam is formed beautifully.
| C | Mn | Si | S | P |
| ≤ 0.12 | 0.3-0.6 | ≤ 0.35 | ≤ 0.035 | ≤ 0.040 |
Mechanical Properties of Deposited Metal:
| Test Item | σ b (MPa) | σ c (MPa) | δ s (%) | AKV(J) |
| Guarantee Value | ≥ 420 | ≥ 330 | ≥ 17 | - |
Recommended Welding Current:
| Electrode Diameter(mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 |
| Current Range(A) | 40-70 | 50-80 | 80-120 | 150-190 | 180-240 |