Audited Supplier
sj101
Solid
Alkaline
Inorganic
>600℃
Sio2+TiO2=15-25
Protect Weld Metal
Submerged-arc Welding
Sintering
EL8, Em12K, Eh14
Lincoln P223 Welding Flux, Esab Ok Flux 10.70
1.Seamless Pipe 2.Struatural Steel
Kraft Bag with Plastic Lining Inside
ISO9001:2008
10-60mesh
120m/Hour
Slag Easy Remove
Welding Powder
PANDING
Kraft Bag with Plastic Lining Inside
25kg/bag, 40bags/plywood pallet
Laiwu, Shandong Pr. China
38109000
Product Description
Chinese high quality Welding Flux SJ101
Equivalnet to LINCOLN P223, ESAB OK FLUX 10.70
1.Specifications:
AWS A5.17/5.23 F6A0-EL8 F6A2-EM12 F7A2-EM12K F7A4-EH14
EN760 SA FB 1 65 AC H5
2.Description:
SJ101 is an agglomerated fluoride-basic type flux. It is gray and round grain,mesh 10-60. it can be operated with AC and DC. ,the welding electric current can up to 1200A.It has excellent weldability, the welding bead appearance is beautiful and the slag is easy to remove. The diffusible hydrogen content in deposited metal is less than 5ml/100g,so it has very good toughness at low temperature,therefore,crack resistance is extremely high. It is suitable for submerged arc twin-wire,tandom and multi-wire welding as well as for welding with the two-run technique.
It should be re-dried under 300-350ºC for 2 hours. Rust,grease and moisture on the weldment should be removed before welding.
3.Applications:
It can be applied to different welding wires(such as H08MnA,H10mN2,H10MnSi,H08Mn2MoA,H08Mn2SiA etc.) It is fit for welding of low-carbon steel and low alloy steel. Such as oil storage tanks,pipeline steel,ships,bridges,pressure vessels,penstocks,boilers and H-beam structural steels.
4.Chemical Composition(%)
5.Mechanical Performance of the Deposited Metal
Attention:
1. We get values in data sheets from tests carried out in accordance to AWS and GB standard procedure. They only represent values we get under those conditions. They are not to be taken as guarantees. AS to welding ,individual test results may depending on experience & technique, flux type, base metal, joint preparation, flux preparation, ampere, voltage, etc.
2. If welding fluxes are stored in improper environment or influenced by condensed moisture, anyway, they get damp, please dry them at 300-350 for 2 hours before usage.
3. Please clean the rust,oil,water on base metal before welding.
4. Add minimum 20% new flux when using recovered flux to avoid welding defects and maintain welding performance & mechanical properties.
5. Please control parameters properly, like preheat temperature, interpass temperature,cooling rate.
Products Picture:
Application:
Factory Introduction:
LAIWU HULIN WELDING MATERIALS CO.,LTD. is top three original factory of Submerged ARC welding flux in China.
Factory was founded in 1994, quality systerm: ISO9001-2008.
Main products: SJ101,SJ101G,SJ301,SJ50,SJ601.HJ431,HJ107,HJ260 etc.
Application: Spiral steel pipe,API pipe, Structural steel, LPC Gas Cylinder, Pressure vessel, Boiler, Bridges etc.
Yearly capacity:30000mt
OEM & buyer label is ok. Technical support can be offered.
FAQ:
Q. 1 Can you provide free sample?
A: Total free sample(including freight cost) can be offered
Q. 2 What is your delivery time?
A: Within 7 days after receiving deposit.
Q: 3 Is your price competitive with other companies?
A: Our goal is to give the best price with same quality and best quality with the same price. We do everything we can to reduce your cost.
Q. 4 How about OEM?
A: OEM IS OK.
Q. 5 Why we should choose your company?
A: Firstly, we are ORIGINAL factory. We can guarantee delivery time and provide special requirements for customers.
Secondly, we have professional foreign trade team with high efficiency communications and professional solutions.
Thirdly, we have special team work for after sales services 24*7 to help you slove any kind of problem
Contact us:
Equivalnet to LINCOLN P223, ESAB OK FLUX 10.70
1.Specifications:
AWS A5.17/5.23 F6A0-EL8 F6A2-EM12 F7A2-EM12K F7A4-EH14
EN760 SA FB 1 65 AC H5
2.Description:
SJ101 is an agglomerated fluoride-basic type flux. It is gray and round grain,mesh 10-60. it can be operated with AC and DC. ,the welding electric current can up to 1200A.It has excellent weldability, the welding bead appearance is beautiful and the slag is easy to remove. The diffusible hydrogen content in deposited metal is less than 5ml/100g,so it has very good toughness at low temperature,therefore,crack resistance is extremely high. It is suitable for submerged arc twin-wire,tandom and multi-wire welding as well as for welding with the two-run technique.
It should be re-dried under 300-350ºC for 2 hours. Rust,grease and moisture on the weldment should be removed before welding.
3.Applications:
It can be applied to different welding wires(such as H08MnA,H10mN2,H10MnSi,H08Mn2MoA,H08Mn2SiA etc.) It is fit for welding of low-carbon steel and low alloy steel. Such as oil storage tanks,pipeline steel,ships,bridges,pressure vessels,penstocks,boilers and H-beam structural steels.
4.Chemical Composition(%)
| SiO2+TiO2 | Al2O3+MnO | CaO+MgO | CaF2 | S | P |
| 15-25 | 20-30 | 25-35 | 25 | ≤0.06 | ≤0.08 |
5.Mechanical Performance of the Deposited Metal
| WIRE | Yield Point Rel(MPa) | Tensile Strength Rm(MPa) | Elongation A (%) | Charpy V Notch Impact Strength KV2(J) | |
| -20ºC | -40ºC | ||||
| EM12 | ≥400 | 465-550 | ≥22 | ≥37 | |
| EM12K | ≥400 | 490-600 | ≥22 | ≥50 | |
| EH14 | ≥400 | 500-650 | ≥22 | ≥70 | ≥50 |
Attention:
1. We get values in data sheets from tests carried out in accordance to AWS and GB standard procedure. They only represent values we get under those conditions. They are not to be taken as guarantees. AS to welding ,individual test results may depending on experience & technique, flux type, base metal, joint preparation, flux preparation, ampere, voltage, etc.
2. If welding fluxes are stored in improper environment or influenced by condensed moisture, anyway, they get damp, please dry them at 300-350 for 2 hours before usage.
3. Please clean the rust,oil,water on base metal before welding.
4. Add minimum 20% new flux when using recovered flux to avoid welding defects and maintain welding performance & mechanical properties.
5. Please control parameters properly, like preheat temperature, interpass temperature,cooling rate.
Products Picture:
Application:
Factory Introduction:
LAIWU HULIN WELDING MATERIALS CO.,LTD. is top three original factory of Submerged ARC welding flux in China.
Factory was founded in 1994, quality systerm: ISO9001-2008.
Main products: SJ101,SJ101G,SJ301,SJ50,SJ601.HJ431,HJ107,HJ260 etc.
Application: Spiral steel pipe,API pipe, Structural steel, LPC Gas Cylinder, Pressure vessel, Boiler, Bridges etc.
Yearly capacity:30000mt
OEM & buyer label is ok. Technical support can be offered.
FAQ:
Q. 1 Can you provide free sample?
A: Total free sample(including freight cost) can be offered
Q. 2 What is your delivery time?
A: Within 7 days after receiving deposit.
Q: 3 Is your price competitive with other companies?
A: Our goal is to give the best price with same quality and best quality with the same price. We do everything we can to reduce your cost.
Q. 4 How about OEM?
A: OEM IS OK.
Q. 5 Why we should choose your company?
A: Firstly, we are ORIGINAL factory. We can guarantee delivery time and provide special requirements for customers.
Secondly, we have professional foreign trade team with high efficiency communications and professional solutions.
Thirdly, we have special team work for after sales services 24*7 to help you slove any kind of problem
Contact us: