Product Description
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=490 | >=18 |
| example value | 564 | 459 | 29 |
Versatile Applications: Specialized for precision automatic submerged arc welding of carbon and low alloy steels, the Honglu Welding Wire is your ideal choice for projects demanding equivalent strength levels, including shipbuilding, petrochemical facilities, and boiler manufacturing.
Outstanding Characteristics: The HH-H10Mn2 copper-plated, non-alloy submerged arc welding wire, combined with SJ101 flux, provides exceptional welding process performance. This pair ensures beautifully shaped weld channels, easy slag removal, and superior low-temperature impact toughness.
Comprehensive Chemical Composition of Our Welding Wire: Composition (mass fraction): A Pure 100%
| sports event | C | Mn | Si | S | P | Cr | Ni | Cu |
| standard value | <=0.12 | 1.50-1.90 | <=0.07 | <=0.030 | <=0.030 | <=0.20 | <=0.30 | <=0.35 |
| example value | 0.11 | 1.65 | 0.05 | 0.017 | 0.022 | 0.022 | 0.02 | 0.116 |
1. Ensure the flux is properly baked at temperatures between 250-400 ºC for 1-2 hours. Keep the welding wire in a dry, oil-free, and rust-free condition before commencing use for optimal results.
2. Thoroughly clean the welding area to remove rust, oil, water, and other impurities before starting the welding process.
3. Maintain sulfur content in the flux at <= 0.050% and phosphorus content at <= 0.060% to ensure high-quality welds.