Product Description
| Type | Rolling Wire |
| Material | 500MPa grade carbon steel wire |
| Flux Containing | Not Containing Flux |
| Extended Length: | >20mm |
| Shielding Gas | CO2 |
| Sep | 0.8, 1.0, 1.2,1.6 |
| Rm/MPa | 490-670 |
| ReL/Rp0.2MPa | >=420 |
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=420 | >=20 |
| example value | 560 | 450 | 26 |
Uses: This exceptional welding wire is engineered for welding carbon steel and low alloy steel structures, making it a versatile solution for industries such as construction machinery, shipbuilding, automotive production, and petrochemical sectors.
Characteristics: The HH-50S-6 wire, tailored for 500MPa level carbon steel, excels with CO2 gas shielded welding. It boasts minimal spatter, flawless shaping, and remarkable deposition efficiency. The wire's minimal porosity sensitivity and outstanding all-position welding capabilities make it an industry favorite.
Mechanical properties of the molten metal: (CO2)
| sports event | C | Mu | Si | S | P | Ni | Cr | Mo | V | Cu |
| standard value | 0.06-0.15 | 1.40-1.85 | 0.80-1.15 | <=0.025 | <=0.025 | <=0.15 | <=0.15 | <=0.15 | <=0.03 | <=0.50 |
| example value | 0.08 | 1.50 | 0.89 | 0.012 | 0.013 | 0.03 | 0.02 | 0.002 | 0.003 | 0.11 |
1. Ensure the weldment is thoroughly free of rust, oil, water, and other contaminants before commencing any welding tasks.
2. The energy size of the welding wire is crucial and directly influences the mechanical properties of the weld. For critical structures, prioritize using smaller wire energy to ensure superior quality and integrity.