Audited Supplier
G-E44
Refractory, Industrial Ceramics
1-10um
95%
Ceramic Part
Ivory, Cream, White, Pink,Yellow,Black
Excellent Wear Resisting
Customized
Excellent Heat / Wear Resistance, Acid Resistance
Production Machinery,Wire Winding, Textile Knittin
with or Without Diamond Polish
Textile, Engineering and Wire Industry
Standard or Customized
99% 95% Alumina,Al2O3,Aluminum Oxide,TiO2,Zro2
Yunnuo
Carton
CUSTOMIZED
China Shanghai
8547100000
Product Description
Textile ceramics are mainly produced from alumina ceramic materials, which have excellent comprehensive technical properties such as high mechanical strength, high hardness, low high-frequency dielectric loss, high temperature insulation resistance, chemical resistance and good thermal conductivity.
Material option:
Steatite
Alumina up to 99.7 % or 95% alumina
Titania
Zirconia
Range of products:
Flange Eyelet, Double flange eyelet, Slotted eyelet, groove eyelets, step eyelet, Cut Eyelet, Step Eyelets, Tubes, Rods, Sleeve,
Ring, Bush, Disc, Dish, Washer, Plates Trap Guide, Traverse Guide, Pig tail Guide, Dog tail Guide, Rollers, Oilers, Oiling Nozzles Cutters
Application :
Yarn manufacturing machines
Twister machines
Airjet looms
Circular looms
weaving machines
winder machines
Rope,Tap plants
Customized guides as per detailed drawings and specifications.
| Item | Unit | 95% al2o3 | 99% al2o3 | Zirconia | Black Tio2 | Yellow Tio2 |
| Color | white,pink | cream,pink | white,black,yellow | Black | Yellow | |
| Density | g/cm3 | 3.65 | 3.9 | 6 | 4 | 4 |
| Flexural strength | MPA | 290 | 390 | 1300 | 70 | 70 |
| Compressive strength | MPA | 3300 | 3900 | 3000 | 600 | 600 |
| Vickers hardness | HV0.5 | 1800 | 2000 | 1150 | 900 | 900 |
| Thermal expansion cofficient | 10-6 K-3 | 5-8.3 | 5.4-8.3 | 10 | 8.5 | 8.5 |
| Thermal conductivity | w/mk | 23 | 28 | 2 | 25 | 25 |