Audited Supplier
HH-ER50S-6
Rolling Wire
CO2
Not Containing Flux
Acidic
>20mm
Accepted
Negotiable; Around 30-35 Days
ISO 9001; CE; RoHS; Reach; OHSAS
200000 Tons
Honglu
0.8; 1.0; 1.2; 1.6
Anhui, China
7505220000
Product Description
| Type | Rolling Wire |
| Material | 500MPa grade carbon steel wire |
| Flux Containing | Not Containing Flux |
| Extended Length: | >20mm |
| Shielding Gas | CO2 |
| Sep | 0.8, 1.0, 1.2,1.6 |
| Rm/MPa | 490-670 |
| ReL/Rp0.2MPa | >=420 |
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=420 | >=20 |
| example value | 560 | 450 | 26 |
Uses: The Versatile Honglu Welding Wire is designed for welding carbon steel and low alloy steel structures with varying strength levels. It is perfectly suited for industries such as construction machinery, shipbuilding, vehicle manufacturing, petrochemicals, and more. This adaptability makes it an essential component for diverse industrial applications.
Characteristics: The HH-50S-6 wire, tailored for 500MPa level carbon steel, utilizes CO2 gas shielded welding to deliver minimal spatter and an aesthetically pleasing finish. It boasts high deposition efficiency with a low sensitivity to weld metal porosity. Additionally, the wire supports an excellent all-position welding process, ensuring reliable performance across various welding scenarios.
Mechanical properties of the molten metal:(CO2)
| sports event | C | Mu | Si | S | P | Ni | Cr | Mo | V | Cu |
| standard value | 0.06-0.15 | 1.40-1.85 | 0.80-1.15 | <=0.025 | <=0.025 | <=0.15 | <=0.15 | <=0.15 | <=0.03 | <=0.50 |
| example value | 0.08 | 1.50 | 0.89 | 0.012 | 0.013 | 0.03 | 0.02 | 0.002 | 0.003 | 0.11 |
1. Prior to welding, ensure the removal of rust, oil, water, and any other impurities from the weldment for optimal results.
2. The energy level of the welding wire is crucial to the mechanical integrity of the weld. Critical structures require lower wire energy levels, enhancing the weld's mechanical properties and ensuring structural reliability.