Product Description
Unsaturated Polyester Resin for Boat Making :
| Item | Type | Promoted/Thix | Viscosity 25ºC Pa.s | Gel Time Min | Non-volatile % | Tensile Strength Mpa | Elongation % | Flexural Strength Mpa | HDT ºC |
| TM-191 | Ortho | Customerize | 0.25-0.45 | 9.0-17.0 | 61.0-67.0 | 64 | 3.6 | 112 | 66 |
| TM-189 | Ortho | Customerize | 0.25-0.45 | 10.5-21.5 | 60.0-66.0 | 61 | 4.6 | 110 | 62 |
| TM-196 | Ortho | Customerize | 0.65-1.15 | 9.1-20.0 | 64.0-70.0 | 72 | 2.5 | 118 | 73 |
| TM-1032 | Ortho | Pre-PRO/ Pre-thiX | 0.34-0.42 | 10.0-30.0 | ----- | 62 | 2 | 118 | 69 |
| TM-107L | Flame | NO | 0.35-0.55 | 15.0-30.0 | 62.0-68.0 | 280 | ---- | 290 | --- |
Gel Coat Resin for Boat Making:
| Item | Type | Color | Accelerator | 25ºC Pa.s Viscosity | Min Gel Time | % Non- volatile | Mpa Flexural Strength | Mpa Tensile Strength | % Elongation | Barcol Hardeness | HDT ºC |
| TM-31 | ISO | Custom erized | Pre-accelerated | 1600-2600/ 3500-5500 | 8-20 | 61.0-67.0 | 120 | 68 | 2.6 | 43 | 81 |
| TM-34 | Ortho | Pre- accelerated | 1600-2600/ 3500-5500 | 8-20 | 60.0-66.0 | 100 | 68 | 2.4 | 46 | 70 | |
| TM-68 | ISO/NPG | Pre- accelerated | 1600-2600/ 3500-5500 | 8-20 | 64.0-70.0 | 125 | 68 | 2.6 | 45 | 90 | |
| TM-52 | Ortho/NPG | Pre- accelerated | 1600-2600/ 3500-5500 | 8-20 | ----- | 105 | 65 | 2.4 | 43 | 68 | |
| TM-31 | ISO | Transp erant | Without | 1600-2600/ 3500-5500 | 8-20 | 61.0-67.0 | 120 | 68 | 2.6 | 43 | 81 |
| TM-34 | Ortho | 1600-2600/ 3500-5500 | 8-20 | 60.0-66.0 | 100 | 68 | 2.4 | 46 | 70 | ||
| TM-68 | ISO/NPG | 1600-2600/ 3500-5500 | 8-20 | 64.0-70.0 | 125 | 68 | 2.6 | 45 | 90 | ||
| TM-52 | Ortho/NPG | 1600-2600/ 3500-5500 | 8-20 | ----- | 105 | 65 | 2.4 | 43 | 68 |
Resin casting matrix performance (for reference only)
Remark:
Casting matrix should follow GB8237-87
Hardness system: hardener 55% MEKPO: 2% ; Accelerator E1:2%
Later Hardness system: 60ºC×2 hours + 120ºC×2 hours
Storage And Transportation
Unsaturated Polyester Resin
GELCOAT RESINS
COLOR PASTE
Yacht:
WORKSHOP:
| Products | Capacity |
| Unsaturated Polyester Resin | 200,000MT |
| Fiberglass Roving | 200,000MT |
| Fiberglass Products | 50000MT |
| Fiberglass binder | 3000MT |
| FRP Products | 1500MT |
| Vinyl Ester Resin | 5000MT |
| Other related Chemcials ,Acceerator,Hardener,Gelcoat | 1000MT |