Fiberglass Chopped Strand Mat: High tensile strength, suitable for use in hand lay-up process
Fiberglass Chopped Strand Mat is made of randomly oriented chopped glass strands around 50mm in length and bonded together with polyester binder in powder form or emulsion form. It is compatible with Polyester, Vinyl ester and Epoxy resin and widely used in boat building, automotive, cooling towers, bathroom accessories, anti-corrosion pipes etc, suitable for hand lay up, filament winding, press molding forming processes.
Features:
1. Randomly dispersed and excellent mechanical properties.
2. Excellent compatibility with resin, cleaning surface, well tightness.
3. Excellent heating resistance.
4. Faster and well resin wet-out rate.
5. Easily fills mold and confirms to complex shapes.
Technical Specification:
Light area weight:
| Property | Area Weight (%) | Moisture Content (%) | Binder Content (%) | Tensile Strength (N/150mm) | Width (mm) |
| Test Method | ISO3374 | ISO3344 | ISO1887 | ISO3342 | ISO 5025 |
| EMC80 | -5.0±10.0 | ≤0.20 | 9±5 | ≥20 | ±5 |
| EMC100 | -5.0±10.0 | ≤0.20 | 9±5 | ≥20 | ±5 |
| EMC120 | -5.0±10.0 | ≤0.20 | 9±5 | ≥20 | ±5 |
Standard area weight:
| Property | Area Weight (%) | Moisture Content (%) | Binder Content (%) | Tensile Strength (N/150mm) | Width (mm) |
| Test Method | ISO3374 | ISO3344 | ISO1887 | ISO3342 | ISO 5025 |
| EMC225 | -5.0±10.0 | ≤0.20 | 4.7±0.9 | ≥30 | ±5 |
| EMC300 | -5.0±10.0 | ≤0.20 | 4.0±0.9 | ≥50 | ±5 |
| EMC450 | -5.0±10.0 | ≤0.20 | 3.7±0.8 | ≥70 | ±5 |
| EMC600 | -5.0±10.0 | ≤0.20 | 3.7±0.8 | ≥80 | ±5 |
| EMC900 | -5.0±10.0 | ≤0.20 | 3.5±0.8 | ≥90 | ±5 |
Products:
Fiberglass roving
Fiberglass products
Unsaturated Polyester Resin
Vinyl Ester Resin
Accelerator /Hardener
FRP products (SMC Sheet, Cooling tower,FRP pipe ,tank)
Therefore Tianma Group Corp has been know as the"cradle of Chinese FRP industry".
Unsaturated polyester resins:
Workshops: