| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=490 | >=18 |
| example value | 564 | 459 | 29 |
A World of Uses: Expertly designed for automatic submerged arc welding, the Honglu Welding Wire is ideal for carbon steel and low alloy steel projects. Perfect for applications demanding corresponding strength levels such as in shipbuilding, petrochemicals, boilers, and many more industries.
Unmatched Characteristics: The HH-H10Mn2 is a premier copper-plated, non-alloy submerged arc welding wire. When paired with SJ101 flux, it boasts exceptional welding process performance, beautiful weld channel shaping, effortless deslagging, and impressive low-temperature impact toughness.
Chemical Composition of Welding Wire: (mass fraction) 100%
| sports event | C | Mn | Si | S | P | Cr | Ni | Cu |
| standard value | <=0.12 | 1.50-1.90 | <=0.07 | <=0.030 | <=0.030 | <=0.20 | <=0.30 | <=0.35 |
| example value | 0.11 | 1.65 | 0.05 | 0.017 | 0.022 | 0.022 | 0.02 | 0.116 |
1. To ensure optimal performance, bake the flux at 250-400 ºC for 1-2 hours. Always use the welding wire in a dry, oil-free, and rust-free state.
2. Prior to welding, meticulously clean to remove rust, oil, water, and any other impurities.
3. Maintain the sulfur content in the flux at <= 0.050% and phosphorus content at <= 0.060% for the best results.