Audited Supplier
E6013
Welding Rod
Low Carbon Steel
Not Containing Flux
Acidic
Provided
5-10 Days
ABS, ISO, CE, CCS, TUV, Lr, BV, Gl, Nk Ect
300mm, 400mm, 450mm
AC and DC
SOLID
5kg/Box, 20kg/Carton, 1000kg/Pallet
2.5mm, 3.2mm, 4.0mm, 4.5mm
Feicheng, Shandong, China
72292000
Product Description
Product Description
Executive standard
GB/T 5117 E4313
AWS A5.1 E6013
ISO 2560-A-E350RA12
Instruction
SLDE4313 is a titanium oxide coated carbon steel rod that can be used for both AC and DC welding in all positions. It has excellent welding process performance, good operational performance, easy arc ignition, and beautiful weld formation.
Application
Suitable for welding steel plates for ships and vehicles, especially for welding thin plates and cover welding that require a beautiful and smooth weld surface.
Chemical composition of deposited metal:(Mass percentage)%
| Item | C | Mn | Si | P | S | Ni | Cr | Mo | V |
| Guarantee Value | ≤0.10 | 0.32-0.55 | ≤0.30 | ≤0.035 | ≤0.030 | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
| Measured Value | 0.07 | 0.37 | 0.22 | 0.016 | 0.024 | 0.05 | 0.025 | 0.007 | 0.009 |
Mechanical properties of deposited metal:
| Item | Rm(MPa) | ReLorRP0.2(MPa) | A(%)(0ºC) | KV2(J) |
| GuaranteeValue | ≥430 | ≥355 | ≥22 | ≥47 |
| MeasuredValue | 490 | 385 | 28 | 76 |
Factory scale
Certifications
ADVANTAGES of Shandong Solid Solder Co.,Ltd.
1. More than 120 production lines for ER70S-6 production
2. About 2000 employee work for this company
3. Established at 1996, more than 18 years experience
4. Varity service, for OEM different products for different brands
5. Certificates for ER70S-6 can meet customers requirements from different country.
6. Deadline: More than 500 tons production each day, your order will be finished in 10~20 days.
7. After sales: any questions about welding wires will be solved at an earliest time.