Product Description
AR water dispersed can be simply added to the mix at the workshop without the need of a special equipment and disperse into filaments in a matrix of calcium silicate slurry,cement slurry etc.
Application:
The 'Premix' production technique involves pouring or pumping a cement/fibre mix into a mould, similar to other precast production processes. The mix is compacted using vibration or by adding other components to the mix. The unit is left in mould to set and demoulded the following day. Pre-mix has the advantages that moulds can be simper to produce and strip
Technical Data
BENEFITS
Excellent alkali resistant and durability
Keeps high integrity during mix
Good fluidity
Packaging&Storage
20kgs /kraft bag, 40bags/800Kg/pallet/109*109*105cm; 50bags /109*109*125cm,20palltes/ 1*20' FCL, N.W.18ton.
Huierjie AR Glassfibre roving pallet shall be stored dry in original packaging and advisable to stack in one layer, at a temperature between 15ºC- 35ºC & relative humidity between 35%- 65%.If stored below 15ºC, it is advisable to hold in workshop for 24 hours to prevent condensation before use.
Note:
Huierjie ARG Fiber are manufactured with high Zirconia rate in compliance with the BSEN 15422:2008 and ASTM C1666/C 1666/M-07 and under the recommendations of GRCA
Application:
The 'Premix' production technique involves pouring or pumping a cement/fibre mix into a mould, similar to other precast production processes. The mix is compacted using vibration or by adding other components to the mix. The unit is left in mould to set and demoulded the following day. Pre-mix has the advantages that moulds can be simper to produce and strip
| PREMIX CODE | WATER DISPERSED CODE |
| ARC15-98-12MML | ARC11-50-12MMD ARC15-98-12MMD |
Technical Data
- Type of glass Alkali Resistant (AR)
- Zirconia (ZrO2) content ≥16.7%
- Filament diameter um 15+2
- Strand tex 98+10
- Elastic modulus 72 Gpa
- Tensile strength 1.4 Gpa
- Length avaiable(MM) 6/12/18/20/24/30/36
- Moisture Content ≤0.2%
- Sizing Content 0.8 - 2.0%
- Breaking strength ≥0.32 N/tex
BENEFITS
Excellent alkali resistant and durability
Keeps high integrity during mix
Good fluidity
Packaging&Storage
20kgs /kraft bag, 40bags/800Kg/pallet/109*109*105cm; 50bags /109*109*125cm,20palltes/ 1*20' FCL, N.W.18ton.
Huierjie AR Glassfibre roving pallet shall be stored dry in original packaging and advisable to stack in one layer, at a temperature between 15ºC- 35ºC & relative humidity between 35%- 65%.If stored below 15ºC, it is advisable to hold in workshop for 24 hours to prevent condensation before use.
Note:
Huierjie ARG Fiber are manufactured with high Zirconia rate in compliance with the BSEN 15422:2008 and ASTM C1666/C 1666/M-07 and under the recommendations of GRCA